THE CHARACTERISTICS OF MICROSTRUCTURES AND PROPERTIES FOR ADVANCED ALUMINUM/SILICON CONTAINED HOT-ROLLED TRIP STEELS
来源期刊：Acta Metallurgica Sinica2004年第6期
论文作者：Q.Liu Y.Chen X.Chen W.Liu P.H.Li G.Y.Tang
Key words：super fine ferrite grain; removable dislocation; retained austenite; aluminum; silicon; hot-rolling; TRIP steel;
Abstract: The microstructure characteristics with super fine ferrite grain size less than 5mm,appropriate retained austenite fraction around 5.0% and or removable abundant dislocations have been obtained by controlled rolling and cooling, which leads to well balance comprehensive properties with high tensile strength of 510 and 615MPa, high elongation of 40% and 27%, low ratio of yield strength to tensile strength 0.83 and 0.80, as well as low ductilebrittle transition temperature less than -80 and -70℃ for advanced aluminum hot-rolled TRIP steel and silicon hot-rolled TRIP steel, respectively.
Q.Liu1，Y.Chen1，X.Chen2，W.Liu1，P.H.Li2，G.Y.Tang1
(1.Graduate School at Shenzhen of Tsinghua University, Shenzhen 518055, China;
2.Wuhan Iron and Steel Group Corporation, Wuhan 430080, China)
Abstract:The microstructure characteristics with super fine ferrite grain size less than 5mm,appropriate retained austenite fraction around 5.0% and or removable abundant dislocations have been obtained by controlled rolling and cooling, which leads to well balance comprehensive properties with high tensile strength of 510 and 615MPa, high elongation of 40% and 27%, low ratio of yield strength to tensile strength 0.83 and 0.80, as well as low ductilebrittle transition temperature less than -80 and -70℃ for advanced aluminum hot-rolled TRIP steel and silicon hot-rolled TRIP steel, respectively.
Key words:super fine ferrite grain; removable dislocation; retained austenite; aluminum; silicon; hot-rolling; TRIP steel;