Effect of niobium on glass-formation ability and soft magnetic properties of Gd-doping glassy alloys
来源期刊：Journal of Rare Earths2008年第1期
论文作者：刘烜 丁艳红 赵水生 龙毅 叶荣昌 常永勤
文章页码：89 - 92
摘 要：The effect of niobium on glass-formation ability and soft magnetic properties were studied in Fe-Gd-B glassy alloys. The glassy alloys exhibited high glass-formation ability when the element of Nb was added. Bulk glassy rod （Fe0.87Co0.13）68.5Gd3.5Nb3B25 with a diameter up to 3 mm was produced by copper mold casting. The size of the atom might play an important role in increasing glass-formation ability. The coercive force of glassy （Fe0.87Co0.13）71.5-xGd3.5NbxB25 （x=1.2, 1.5, 2, 2.5, 3, 4） alloys decreased after the addition of niobium element and was in the range of 1.5-2.9 A/m. The permeability spectrum of （Fe0.87Co0.13）70.3Gd3.5Nb1.5B25 glassy ribbon showed that the relaxation fre- quency （f0） was 6.1 MHz.
刘烜，丁艳红，赵水生，龙毅，叶荣昌，常永勤
摘 要：The effect of niobium on glass-formation ability and soft magnetic properties were studied in Fe-Gd-B glassy alloys. The glassy alloys exhibited high glass-formation ability when the element of Nb was added. Bulk glassy rod （Fe0.87Co0.13）68.5Gd3.5Nb3B25 with a diameter up to 3 mm was produced by copper mold casting. The size of the atom might play an important role in increasing glass-formation ability. The coercive force of glassy （Fe0.87Co0.13）71.5-xGd3.5NbxB25 （x=1.2, 1.5, 2, 2.5, 3, 4） alloys decreased after the addition of niobium element and was in the range of 1.5-2.9 A/m. The permeability spectrum of （Fe0.87Co0.13）70.3Gd3.5Nb1.5B25 glassy ribbon showed that the relaxation fre- quency （f0） was 6.1 MHz.
关键词：