Time-stability of sintered Nd-Fe-B permanent magnet with lower oxygen content
来源期刊：JOURNAL OF RARE EARTHS2010年第S1期
论文作者：刘国征 夏宁 赵明静 李波 喻晓军
文章页码：396 - 398
摘 要：Time-stability of sintered Nd-Fe-B magnet with lower content of oxygen at different temperatures and humidity conditions for 400 d was investigated.Results showed that the magnetic flux loss was-0.68% for the non-electroplating samples and-0.43% for the electroplating samples at room temperature and average humidity was 25% during 400 d,respectively.The magnetic flux loss of the plated samples was lower than non-plated samples under the conditions of room temperature and with the average humidity of 54%,but the magnetic flux loss of the plated samples was larger than that of the non-plated sample at 80 oC.The magnetic flux loss of electroplated and non-electroplated sintered Nd-Fe-B magnets was less than 1% for 400 d,which showed that the N40SH grade magnets have good time stability.
刘国征1,2，夏宁1，赵明静1，李波2，喻晓军2
1. Research Center of Functional Materials,Baotou Research Institute of Rare Earth2. Department of Functional Materials,Advanced Technology and Materials,China Iron & Steel Research Institute Group
摘 要：Time-stability of sintered Nd-Fe-B magnet with lower content of oxygen at different temperatures and humidity conditions for 400 d was investigated.Results showed that the magnetic flux loss was-0.68% for the non-electroplating samples and-0.43% for the electroplating samples at room temperature and average humidity was 25% during 400 d,respectively.The magnetic flux loss of the plated samples was lower than non-plated samples under the conditions of room temperature and with the average humidity of 54%,but the magnetic flux loss of the plated samples was larger than that of the non-plated sample at 80 oC.The magnetic flux loss of electroplated and non-electroplated sintered Nd-Fe-B magnets was less than 1% for 400 d,which showed that the N40SH grade magnets have good time stability.
关键词：