论文作者：Anbarasu Venugopalan Manigandan Appasamy Sathiyakumar Saravanan Kaliyaperumal Kothandaraman Jayabalan Kothandaraman
文章页码：1013 - 1017
摘 要：The compounds of iron substituted yttrium oxide systems have been prepared for the importance in the field of magneto electric materials.The polycrystalline samples of Y2-xFexO3-y（x=0.1,0.2） were prepared by solid-state reaction method.The single-phase formation of these compounds was confirmed by X-ray diffraction studies.It was found that the samples crystallized in tetragonal phase and the lattice parameters were calculated as a=1.0559（7） nm,c=1.0832（9） nm for Y1.9Fe0.1O3-y and a=1.0545（6） nm,c=1.0841（8） nm for Y1.8Fe0.2O3-y.The lattice constant changed with the variation of Fe concentration,which indicated the incorporation of Fe3+ into the hosting Y2O3.The semi conducting nature of the prepared compounds was observed with the energy gap calculation from diffused reflectance spectroscopy（DRS） studies.The ferromagnetic nature of the prepared compounds was identified with vibrating sample magnetometer studies.This information were corroborated by the observation of the well broadened EPR lines in the electron paramagnetic resonance（EPR） spectra of the samples with a low Fe concentration,which manifested the onset of Fe-Fe exchange interaction in the prepared samples.
Anbarasu Venugopalan1，Manigandan Appasamy1，Sathiyakumar Saravanan1，Kaliyaperumal Kothandaraman2，Jayabalan Kothandaraman1
1. Department of Physics,Anna University2. Department of Physics,Pondicherry Engineering College
摘 要：The compounds of iron substituted yttrium oxide systems have been prepared for the importance in the field of magneto electric materials.The polycrystalline samples of Y2-xFexO3-y（x=0.1,0.2） were prepared by solid-state reaction method.The single-phase formation of these compounds was confirmed by X-ray diffraction studies.It was found that the samples crystallized in tetragonal phase and the lattice parameters were calculated as a=1.0559（7） nm,c=1.0832（9） nm for Y1.9Fe0.1O3-y and a=1.0545（6） nm,c=1.0841（8） nm for Y1.8Fe0.2O3-y.The lattice constant changed with the variation of Fe concentration,which indicated the incorporation of Fe3+ into the hosting Y2O3.The semi conducting nature of the prepared compounds was observed with the energy gap calculation from diffused reflectance spectroscopy（DRS） studies.The ferromagnetic nature of the prepared compounds was identified with vibrating sample magnetometer studies.This information were corroborated by the observation of the well broadened EPR lines in the electron paramagnetic resonance（EPR） spectra of the samples with a low Fe concentration,which manifested the onset of Fe-Fe exchange interaction in the prepared samples.
关键词：