Biodegradable Zn–3Cu and Zn–3Cu–0.2Ti alloys with ultrahigh ductility and antibacterial ability for orthopedic applications
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG2021年第9期
论文作者：Jixing Lin Xian Tong Kun Wang Zimu Shi Yuncang Li Matthew Dargusch Cuie Wen
文章页码：76 - 90
摘 要：Zinc（Zn） and its alloys have been proposed as biodegradable implant materials due to their unique combination of biodegradability, biocompatibility, and biofunctionality. However, the insufficient mechanical properties of pure Zn greatly limit its clinical application. Here, we report on the microstructure, mechanical properties, friction and wear behavior, corrosion and degradation properties, hemocompatibility, and cytocompatibility of Zn–3 Cu and Zn–3 Cu–0.2 Ti alloys under three different conditions of as-cast（AC）,hot-rolling（HR）, and hot-rolling plus cold-rolling（HR + CR）. The HR + CR Zn–3 Cu–0.2 Ti exhibited the best set of comprehensive properties among all the alloy samples, with yield strength of 211.0 MPa, ultimate strength of 271.1 MPa, and elongation of 72.1 %. Immersion tests of the Zn–3 Cu and Zn–3 Cu–0.2 Ti alloys in Hanks’ solution for 3 months indicated that the AC samples showed the lowest degradation rate,followed by the HR samples, and then the HR + CR samples, while the HR + CR Zn–3 Cu exhibited the highest degradation rate of 23.9 m/a. Friction and wear testing of the Zn–3 Cu and Zn–3 Cu–0.2 Ti alloys in Hanks’ solution indicated that the AC samples showed the highest wear resistance, followed by the HR samples, and then the HR + CR samples, while the AC Zn–3 Cu–0.2 Ti showed the highest wear resistance.The diluted extracts of HR + CR Zn–3 Cu and Zn–3 Cu–0.2 Ti at a concentration of ≤25 % exhibited noncytotoxicity. Furthermore, both the HR + CR Zn–3 Cu and Zn–3 Cu–0.2 Ti exhibited effective antibacterial properties against S. aureus.
Jixing Lin1，Xian Tong1,2，Kun Wang1，Zimu Shi3，Yuncang Li4，Matthew Dargusch5，Cuie Wen4
1. Department of Material Engineering, Zhejiang Industry & Trade Vocational College2. School of Materials Science and Engineering, Xiangtan University3. Key Laboratory of Materials Physics, Institute of Solid State Physics, Chinese Academy of Sciences4. School of Engineering, RMIT University5. Centre for Advanced Materials Processing and Manufacturing (AMPAM), The University of Queensland
摘 要：Zinc（Zn） and its alloys have been proposed as biodegradable implant materials due to their unique combination of biodegradability, biocompatibility, and biofunctionality. However, the insufficient mechanical properties of pure Zn greatly limit its clinical application. Here, we report on the microstructure, mechanical properties, friction and wear behavior, corrosion and degradation properties, hemocompatibility, and cytocompatibility of Zn–3 Cu and Zn–3 Cu–0.2 Ti alloys under three different conditions of as-cast（AC）,hot-rolling（HR）, and hot-rolling plus cold-rolling（HR + CR）. The HR + CR Zn–3 Cu–0.2 Ti exhibited the best set of comprehensive properties among all the alloy samples, with yield strength of 211.0 MPa, ultimate strength of 271.1 MPa, and elongation of 72.1 %. Immersion tests of the Zn–3 Cu and Zn–3 Cu–0.2 Ti alloys in Hanks’ solution for 3 months indicated that the AC samples showed the lowest degradation rate,followed by the HR samples, and then the HR + CR samples, while the HR + CR Zn–3 Cu exhibited the highest degradation rate of 23.9 m/a. Friction and wear testing of the Zn–3 Cu and Zn–3 Cu–0.2 Ti alloys in Hanks’ solution indicated that the AC samples showed the highest wear resistance, followed by the HR samples, and then the HR + CR samples, while the AC Zn–3 Cu–0.2 Ti showed the highest wear resistance.The diluted extracts of HR + CR Zn–3 Cu and Zn–3 Cu–0.2 Ti at a concentration of ≤25 % exhibited noncytotoxicity. Furthermore, both the HR + CR Zn–3 Cu and Zn–3 Cu–0.2 Ti exhibited effective antibacterial properties against S. aureus.
关键词：