Effects of calcium, samarium addition on microstructure and mechanical properties of AZ61 magnesium alloy
来源期刊：JOURNAL OF RARE EARTHS2015年第1期
论文作者：陈玉安 金李 方丹 宋裕 叶睿宇
文章页码：86 - 92
摘 要：The microstructure and mechanical properties of AZ61 magnesium alloy with Ca, Sm addition were investigated. The results showed that the addition of 0.5 wt.% Ca reduced the quantity of Mg17Al12 phase, and formed a new Al4 Ca phase which is reticular in AZ61 alloy. With the addition of Ca and Sm, the microstructure was further refined and new Al-Sm rich phases were formed in AZ61 alloy with 0.6 wt.%–1.5 wt.% Sm addition, the TEM analysis confirmed that they were Al2 Sm and Al4 Sm. Tensile tests showed that 1.0 wt.% Sm addition contributed to the formation of the Al2 Sm and Al4 Sm and the improvement in the ambient strength, i.e., an ultimate tensile strength of 327 MPa and an elongation of 10.1%. However, excessive Sm addition led to the coarsening of Al2 Sm and Al4 Sm phases, thus resulted in the decline of strength and plasticity.
陈玉安，金李，方丹，宋裕，叶睿宇
College of Materials Science and Engineering, Chongqing University
摘 要：The microstructure and mechanical properties of AZ61 magnesium alloy with Ca, Sm addition were investigated. The results showed that the addition of 0.5 wt.% Ca reduced the quantity of Mg17Al12 phase, and formed a new Al4 Ca phase which is reticular in AZ61 alloy. With the addition of Ca and Sm, the microstructure was further refined and new Al-Sm rich phases were formed in AZ61 alloy with 0.6 wt.%–1.5 wt.% Sm addition, the TEM analysis confirmed that they were Al2 Sm and Al4 Sm. Tensile tests showed that 1.0 wt.% Sm addition contributed to the formation of the Al2 Sm and Al4 Sm and the improvement in the ambient strength, i.e., an ultimate tensile strength of 327 MPa and an elongation of 10.1%. However, excessive Sm addition led to the coarsening of Al2 Sm and Al4 Sm phases, thus resulted in the decline of strength and plasticity.
关键词：