Cathodoluminescent properties of Tb3+-doped yttria nanocrystallites
来源期刊:Journal of Rare Earths2009年第4期
论文作者:P.Psuja D.Hreniak W.Strek
文章页码:574 - 578
摘 要:The Tb3+-doped Y2O3 nanopowders were synthesized using the modified Pechini method. The average size of nanocrystallites was controlled by different sintering temperatures. The structure and morphology of obtained nanopowders were examined using the XRD and SEM analyses. The Cr:Al2O3 was mixed with Tb3+:Y2O3 powders and its normalized emission was used to measure a relative intensity of Tb3+:Y2O3. The mixtures were electrophoretically deposited on ITO-glass slides. The cathodoluminescence spectra of obtained layers were recorded and analysed. The discussion over an influence of average grains size on phosphor efficiency was presented.
P.Psuja,D.Hreniak,W.Strek
Institute of Low Temperature and Structure Research, Polish Academy of Sciences ul.Okolna 2, 50-422 Wroclaw, Poland
摘 要:The Tb3+-doped Y2O3 nanopowders were synthesized using the modified Pechini method. The average size of nanocrystallites was controlled by different sintering temperatures. The structure and morphology of obtained nanopowders were examined using the XRD and SEM analyses. The Cr:Al2O3 was mixed with Tb3+:Y2O3 powders and its normalized emission was used to measure a relative intensity of Tb3+:Y2O3. The mixtures were electrophoretically deposited on ITO-glass slides. The cathodoluminescence spectra of obtained layers were recorded and analysed. The discussion over an influence of average grains size on phosphor efficiency was presented.
关键词: