EFFECT OF BRAZING TIME ON TiC CERMET/IRON JOINT BRAZED WITH Ag-Cu-Zn FILLER METAL
来源期刊：Acta Metallurgica Sinica2004年第1期
论文作者：J.C.Feng Z.R.Li L.X.Zhang H.J.Liu
Key words：brazing; TiC cermet; interface; shear strength;
Abstract: The brazing of TiC cermet to iron was carried out at 1223K for 5-20min using Ag-Cu-Zn filler metal. The formation phase and interface structure of the joints were investigated by electron probe microanalysis (EPMA), scanning electron microscopy (SEM) and X-ray diffraction (XRD), and the joint strength was tested by shearing method. The results showed: there occurred three new formation phases, Cu(s.s), FeNi and Ag(s.s) in TiC cermet/iron joint. The interface structure was expressed as TiC cermet/Cu(s.s)+FeNi/Ag(s.s)+a little Cu(s.s)+a little FeNi/Cu(s.s)+ FeNi/iron. With brazing time increasing, there appeared highest shear strength of the joints, the value of which was up to 252.2MPa when brazing time was 10min.
J.C.Feng1，Z.R.Li1，L.X.Zhang1，H.J.Liu1
(1.National Key Laboratory of Advanced Welding Production Technology, Harbin Institute of Technology,Harbin 150001, China)
Abstract:The brazing of TiC cermet to iron was carried out at 1223K for 5-20min using Ag-Cu-Zn filler metal. The formation phase and interface structure of the joints were investigated by electron probe microanalysis (EPMA), scanning electron microscopy (SEM) and X-ray diffraction (XRD), and the joint strength was tested by shearing method. The results showed: there occurred three new formation phases, Cu(s.s), FeNi and Ag(s.s) in TiC cermet/iron joint. The interface structure was expressed as TiC cermet/Cu(s.s)+FeNi/Ag(s.s)+a little Cu(s.s)+a little FeNi/Cu(s.s)+ FeNi/iron. With brazing time increasing, there appeared highest shear strength of the joints, the value of which was up to 252.2MPa when brazing time was 10min.
Key words:brazing; TiC cermet; interface; shear strength;
【全文内容正在添加中】