Preparation of YAG Powder by Co-Precipitation Method in a Narrow pH-Change Environment

来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2010年第3期

论文作者:马奔原 卢铁城

文章页码:379 - 383

摘    要:YAG(Y3Al5O12) powder was prepared by co-precipitation method.To avoid pH values changing intensely during titration process,the 4 3 NH HCO solution with 4 3 NH NO was used as precipitant solution.The pH change of precipitant solution during titration process,compositions of precursor,phase formation process and morphology of the prepared powder were investigated by means of pH meter,FT-IR,XRD and TEM.The results show that the presence of 4 3 NH NO in 4 3 NH HCO solution is crucial to alleviate the pH change,lower the calcination temperature and meliorate the morphology of YAG powder.The mechanisms were studied in detail.The YAG phase can be obtained at a lower temperature of 900 ℃.The obtained powder,composed of elliptical particles,showed a meliorated morphology.

详情信息展示

Preparation of YAG Powder by Co-Precipitation Method in a Narrow pH-Change Environment

马奔原1,卢铁城1,2

1. Department of Physics and Key Laboratory for Radiation Physics and Technology of Ministry of Education,Sichuan University2. International Center for Material Physics,Chinese Academy of Sciences

摘 要:YAG(Y3Al5O12) powder was prepared by co-precipitation method.To avoid pH values changing intensely during titration process,the 4 3 NH HCO solution with 4 3 NH NO was used as precipitant solution.The pH change of precipitant solution during titration process,compositions of precursor,phase formation process and morphology of the prepared powder were investigated by means of pH meter,FT-IR,XRD and TEM.The results show that the presence of 4 3 NH NO in 4 3 NH HCO solution is crucial to alleviate the pH change,lower the calcination temperature and meliorate the morphology of YAG powder.The mechanisms were studied in detail.The YAG phase can be obtained at a lower temperature of 900 ℃.The obtained powder,composed of elliptical particles,showed a meliorated morphology.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号