Hot deformation behavior and microstructure evolution of a Mg–Gd–Nd–Y–Zn alloy
来源期刊：Rare Metals2016年第7期
论文作者：Xiu-Li Hou Yan Li Peng Lv Jie Cai Le Ji Qing-Feng Guan
文章页码：532 - 536
摘 要：The hot deformation behavior of homogenized Mg–6.5Gd–1.3Nd–0.7Y–0.3Zn alloy was investigated during compression at temperatures of 250–400 ℃ and at strain rates ranging from 0.001 to 0.100 s-1. Microstructure analyses show that the flow behaviors are associated with the deformation mechanisms. At the lower temperatures（250–300 ℃）, deformation twinning is triggered due to the difficult activation of dislocation cross-slip. Dynamic recrystallization（DRX） accompanied by dynamic precipitation occurs at the temperature of 350 ℃ and influences the softening behavior of the flow.DRX that develops extensively at original grain boundaries is the main softening mechanism at the high temperature of 400 ℃ and eventually brings a more homogeneous microstructure than that in other deformation conditions. The volume fraction of the DRXed grains increases with temperature increasing and decreases with strain rate increasing.
Xiu-Li Hou，Yan Li，Peng Lv，Jie Cai，Le Ji，Qing-Feng Guan
School of Materials Science and Engineering,Jiangsu University
摘 要：The hot deformation behavior of homogenized Mg–6.5Gd–1.3Nd–0.7Y–0.3Zn alloy was investigated during compression at temperatures of 250–400 ℃ and at strain rates ranging from 0.001 to 0.100 s-1. Microstructure analyses show that the flow behaviors are associated with the deformation mechanisms. At the lower temperatures（250–300 ℃）, deformation twinning is triggered due to the difficult activation of dislocation cross-slip. Dynamic recrystallization（DRX） accompanied by dynamic precipitation occurs at the temperature of 350 ℃ and influences the softening behavior of the flow.DRX that develops extensively at original grain boundaries is the main softening mechanism at the high temperature of 400 ℃ and eventually brings a more homogeneous microstructure than that in other deformation conditions. The volume fraction of the DRXed grains increases with temperature increasing and decreases with strain rate increasing.
关键词：