Development of bulk metallic glasses based on the Dy-Al binary eutectic composition
来源期刊：Journal of Rare Earths2008年第6期
论文作者：罗林 田瑞 肖学山
文章页码：813 - 816
摘 要：<正>A series of dysprosium-based ternary, quadruple, and quintuple bulk metallic glasses （BMGs） based on Dy-Al binary eutectic compo-sition were obtained with the partial substitution of Co, Gd, and Ni elements, for dysprosium. The results showed that the Dy31Gd25Co20Al24 alloy, which had the best glass forming ability （GFA）, could be cast into an amorphous rod with a diameter of 5 mm. The GFA of alloys was evaluated on the basis of the supercooled liquid region width, γ parameter, the formation enthalpy, and the equivalent electronegativity difference of amor-phous alloys. It was found that the eutectic composition was closely correlated with the GFA of the Dy-based BMGs.
罗林，田瑞，肖学山
摘 要：<正>A series of dysprosium-based ternary, quadruple, and quintuple bulk metallic glasses （BMGs） based on Dy-Al binary eutectic compo-sition were obtained with the partial substitution of Co, Gd, and Ni elements, for dysprosium. The results showed that the Dy31Gd25Co20Al24 alloy, which had the best glass forming ability （GFA）, could be cast into an amorphous rod with a diameter of 5 mm. The GFA of alloys was evaluated on the basis of the supercooled liquid region width, γ parameter, the formation enthalpy, and the equivalent electronegativity difference of amor-phous alloys. It was found that the eutectic composition was closely correlated with the GFA of the Dy-based BMGs.
关键词：