Electromagnetic and microwave absorbing properties of W-type barium ferrite doped with Gd3+

来源期刊:Rare Metals2011年第1期

论文作者:HUANG Xiaogua,CHEN Jiaoa,WANG Lixia,and ZHANG Qitua,b a College of Materials Science and Engineering,Nanjing University of Technology,Nanjing ,China b Jiangsu Provincial Key Laboratory of Inorganic and Composite New Materials,Nanjing University of Technology,Nanjing ,China

文章页码:44 - 48

摘    要:W-type barium ferrites doped with Gd3+,Ba1-xGdx(Zn0.3Co0.7)2Fe16O27(x = 0,0.05,0.10,0.15,0.20),were prepared by a sol-gel method.The effects of Gd3+ substitution on their microstructure,electromagnetic properties and microwave absorptive behavior were analyzed.The XRD patterns showed the single phase of W-type barium ferrite when x ≤ 0.15.Microwave electromagnetic properties of samples were studied at the frequency range from 2 GHz to 18 GHz using a network analyzer(Agilent 8722ET).The complex permittivity ε(ε’,ε’’) increased gradually when x ≤ 0.10,but it decreased as x = 0.15.The real permeability(μ’) decreased with the increase of Gd3+ content,while the imaginary permeability(μ’’) increased when x ≤ 0.10.All these reasons were discussed using the electromagnetic theory.Furthermore,the ferrite-epoxy compound coating materials with 80 wt.% of Ba0.9Gd0.1(Zn0.3Co0.7)2Fe16O27 were prepared to measure the microwave absorbing properties.The maximum of reflection loss(RL) reached about-27 dB and RL was below-10 dB in the frequency range of 8-18 GHz when the thickness was 1.92 mm.

详情信息展示

Electromagnetic and microwave absorbing properties of W-type barium ferrite doped with Gd3+

HUANG Xiaogua,CHEN Jiaoa,WANG Lixia,and ZHANG Qitua,b a College of Materials Science and Engineering,Nanjing University of Technology,Nanjing 210009,China b Jiangsu Provincial Key Laboratory of Inorganic and Composite New Materials,Nanjing University of Technology,Nanjing 210009,China

摘 要:W-type barium ferrites doped with Gd3+,Ba1-xGdx(Zn0.3Co0.7)2Fe16O27(x = 0,0.05,0.10,0.15,0.20),were prepared by a sol-gel method.The effects of Gd3+ substitution on their microstructure,electromagnetic properties and microwave absorptive behavior were analyzed.The XRD patterns showed the single phase of W-type barium ferrite when x ≤ 0.15.Microwave electromagnetic properties of samples were studied at the frequency range from 2 GHz to 18 GHz using a network analyzer(Agilent 8722ET).The complex permittivity ε(ε’,ε’’) increased gradually when x ≤ 0.10,but it decreased as x = 0.15.The real permeability(μ’) decreased with the increase of Gd3+ content,while the imaginary permeability(μ’’) increased when x ≤ 0.10.All these reasons were discussed using the electromagnetic theory.Furthermore,the ferrite-epoxy compound coating materials with 80 wt.% of Ba0.9Gd0.1(Zn0.3Co0.7)2Fe16O27 were prepared to measure the microwave absorbing properties.The maximum of reflection loss(RL) reached about-27 dB and RL was below-10 dB in the frequency range of 8-18 GHz when the thickness was 1.92 mm.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号