Extraction and characterization of alumina nanopowders from aluminum dross by acid dissolution process

来源期刊:International Journal of Minerals Metallurgy and Materials2015年第4期

论文作者:Saifur Rahman Sarker Zahangir Alam

文章页码:429 - 436

摘    要:A significant amount of aluminum dross is available as a waste in foundry industries in Bangladesh. In this study, alumina was extracted from aluminum dross collected from two foundry industries situated in Dhamrai and Manikgang, near the capital city, Dhaka. Aluminum dross samples were found to approximately contain 75wt% Al2O3 and 12wt% SiO2. An acid dissolution process was used to recover the alumina value from the dross. The effects of various parameters, e.g., temperature, acid concentration, and leaching time, on the extraction of alumina were studied to optimize the dissolution process. First, Al(OH)3 was produced in the form of a gel. Calcination of the Al(OH)3 gel at 1000°C, 1200°C, and 1400°C for 2 h produced θ-Al2O3,(α+θ)-Al2O3, and α-alumina powder, respectively. Thermal characterization of the Al(OH)3 gel was performed by thermogravimetric/differential thermal analysis(TG/DTA) and differential scanning calorimetry(DSC). The phases and crystallite size of the alumina were determined by X-ray diffraction analysis. The dimensions of the alumina were found to be on the nano level. The chemical compositions of the aluminum dross and alumina were determined by X-ray fluorescence(XRF) spectroscopy. The microstructure and morphology of the alumina were studied with scanning electron microscopy. The purity of the alumina extracted in this study was found to be 99.0%. Thus, it is expected that the obtained alumina powders can be potentially utilized as biomaterials.

详情信息展示

Extraction and characterization of alumina nanopowders from aluminum dross by acid dissolution process

Saifur Rahman Sarker1,Zahangir Alam1

1. Department of Applied Chemistry and Chemical Engineering University of Dhaka

摘 要:A significant amount of aluminum dross is available as a waste in foundry industries in Bangladesh. In this study, alumina was extracted from aluminum dross collected from two foundry industries situated in Dhamrai and Manikgang, near the capital city, Dhaka. Aluminum dross samples were found to approximately contain 75wt% Al2O3 and 12wt% SiO2. An acid dissolution process was used to recover the alumina value from the dross. The effects of various parameters, e.g., temperature, acid concentration, and leaching time, on the extraction of alumina were studied to optimize the dissolution process. First, Al(OH)3 was produced in the form of a gel. Calcination of the Al(OH)3 gel at 1000°C, 1200°C, and 1400°C for 2 h produced θ-Al2O3,(α+θ)-Al2O3, and α-alumina powder, respectively. Thermal characterization of the Al(OH)3 gel was performed by thermogravimetric/differential thermal analysis(TG/DTA) and differential scanning calorimetry(DSC). The phases and crystallite size of the alumina were determined by X-ray diffraction analysis. The dimensions of the alumina were found to be on the nano level. The chemical compositions of the aluminum dross and alumina were determined by X-ray fluorescence(XRF) spectroscopy. The microstructure and morphology of the alumina were studied with scanning electron microscopy. The purity of the alumina extracted in this study was found to be 99.0%. Thus, it is expected that the obtained alumina powders can be potentially utilized as biomaterials.

关键词:

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号