Preparation and characterization of Ce0.8La0.2–xYxO1.9 as electrolyte for solid oxide fuel cells
来源期刊：JOURNAL OF RARE EARTHS2014年第12期
论文作者：田长安 季必发 谢劲松 鲍巍涛 刘可 程继海 尹奇异
文章页码：1162 - 1169
摘 要：In this study, ultrafine Ce0.8La0.2–x Y x O1.9（for x=0, 0.05, 0.10, 0.15, 0.20） powders were successfully prepared by the sol-gel method.The samples were characterized by fourier transform infrared（FTIR）, thermogravimetric and differential scanning calorimetry（TG-DSC）, X-ray diffraction（XRD）, scanning electron microscopy（SEM）, AC impedance and thermal expansion measurements.Experimental results indicated that highly phase-pure cubic fluorite electrolyte Ce0.8La0.2–x Y x O1.9 powders were obtained after calcining at 600 °C.The as-synthesized powders exhibited high sintering activity, the Ce0.8La0.2–x Y x O1.9 series electrolytes which have higher relative densities over 96% could be obtained after sintered at 1400 °C for 4 h.Ce0.8La0.15Y0.05O1.9 electrolyte sintered at 1400 °C for 4 h exhibited higher oxide ionic conductivity（σ800 oC=0.057 S/cm）, lower electrical activation energy（E a=0.87 e V） and moderate thermal expansion coefficient（TEC=15.5×10-6 K-1, temperature range 25–800 °C）.
田长安，季必发，谢劲松，鲍巍涛，刘可，程继海，尹奇异
Department of Chemistry and Materials Engineering, Hefei University
摘 要：In this study, ultrafine Ce0.8La0.2–x Y x O1.9（for x=0, 0.05, 0.10, 0.15, 0.20） powders were successfully prepared by the sol-gel method.The samples were characterized by fourier transform infrared（FTIR）, thermogravimetric and differential scanning calorimetry（TG-DSC）, X-ray diffraction（XRD）, scanning electron microscopy（SEM）, AC impedance and thermal expansion measurements.Experimental results indicated that highly phase-pure cubic fluorite electrolyte Ce0.8La0.2–x Y x O1.9 powders were obtained after calcining at 600 °C.The as-synthesized powders exhibited high sintering activity, the Ce0.8La0.2–x Y x O1.9 series electrolytes which have higher relative densities over 96% could be obtained after sintered at 1400 °C for 4 h.Ce0.8La0.15Y0.05O1.9 electrolyte sintered at 1400 °C for 4 h exhibited higher oxide ionic conductivity（σ800 oC=0.057 S/cm）, lower electrical activation energy（E a=0.87 e V） and moderate thermal expansion coefficient（TEC=15.5×10-6 K-1, temperature range 25–800 °C）.
关键词：