Effect of Sm-rich liquid phase on magnetic properties and microstructures of sintered 2:17-type Sm-Co magnet
来源期刊：Journal of Rare Earths2011年第10期
论文作者：张文臣 赵睿 方以坤 周鸣鸽 朱明刚 李卫
文章页码：934 - 938
摘 要：The effect of Sm-rich liquid phase（Sm2Co3） on magnetic properties and microstructure of 2:17-type Sm-Co magnet was studied.Three phases existed in liquid phase ingot,and took on white,dark grey and grey,respectively.It was found that the composition of the greyarea was similar to the nominal one.Our results indicated that the optimal composition was obtained at 3 wt.% liquid phase added,and themagnetic properties were Br=11.58 kGs,Hci>26 kOe,（BH）m=29.51 MGOe.Br increased by 3%,Hci was 13 times larger,and（BH）m was 6times bigger than none liquid phase magnets.Moreover,with the aging time decreasing from 20 to 8 h,the squareness of the demagnetizationcurves got better,while the coercivity of the samples decreased.It revealed that Sm（Co,Cu）5 phase also precipitated at particle boundaries.Itmaybe also enhanced the coercivity.
张文臣，赵睿，方以坤，周鸣鸽，朱明刚，李卫
Division of Functional Materials,Central Iron and Steel Research Institute
摘 要：The effect of Sm-rich liquid phase（Sm2Co3） on magnetic properties and microstructure of 2:17-type Sm-Co magnet was studied.Three phases existed in liquid phase ingot,and took on white,dark grey and grey,respectively.It was found that the composition of the greyarea was similar to the nominal one.Our results indicated that the optimal composition was obtained at 3 wt.% liquid phase added,and themagnetic properties were Br=11.58 kGs,Hci>26 kOe,（BH）m=29.51 MGOe.Br increased by 3%,Hci was 13 times larger,and（BH）m was 6times bigger than none liquid phase magnets.Moreover,with the aging time decreasing from 20 to 8 h,the squareness of the demagnetizationcurves got better,while the coercivity of the samples decreased.It revealed that Sm（Co,Cu）5 phase also precipitated at particle boundaries.Itmaybe also enhanced the coercivity.
关键词：