Properties of Al/Conductive Coating/α-PbO2-CeO2-TiO2/β-PbO2-WC-ZrO2 Composite Anode for Zinc Electrowinning
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2017年第3期
论文作者：杨健 陈步明 GUO Zhongcheng HUANG Hui XU Ruidong JIN Bingjie
文章页码：538 - 546
摘 要：The properties of Al/conductive coating/α-PbO2-CeO2-TiO2/β-PbO2-WC-ZrO2 composite anode for zinc electrowinning were investigated. The electrochemical performance was studied by Tafel polarization curves（Tafel）, electrochemical impedance spectroscopy（EIS） and corrosion rate obtained in an acidic zinc sulfate electrolyte solution. Scanning electron microscopy（SEM）, X-ray diffraction（XRD）, and energy dispersive X-ray spectroscopy（EDXS） were used to observe the microstructural features of coating. Anodes of Al/conductive coating/α-PbO2-CeO2-TiO2/β-PbO2, Al/conductive coating/α-PbO2-CeO2-TiO2/β-PbO2-WC, Al/conductive coating/α-PbO2-CeO2-TiO2/β-PbO2-ZrO2, and Pb-1%Ag anodes were also researched. The results indicated that the Al/conductive coating/α-PbO2-CeO2-TiO2/β-PbO2-WC-ZrO2 showed the best catalytic activity and corrosion resistant performance; the intensity of diffraction peak exhibited the highest value as well as a new PbWO4 phase; the content of WC and ZrO2 in coating showed the highest value as well as the finest grain size.
杨健1，陈步明1，GUO Zhongcheng1,2，HUANG Hui1，XU Ruidong1，JIN Bingjie1
1. Faculty of Metallurgical and Energy Engineering, Kunming University of Science and Technology2. Kunming Hendera Science and Technology Co.Ltd
摘 要：The properties of Al/conductive coating/α-PbO2-CeO2-TiO2/β-PbO2-WC-ZrO2 composite anode for zinc electrowinning were investigated. The electrochemical performance was studied by Tafel polarization curves（Tafel）, electrochemical impedance spectroscopy（EIS） and corrosion rate obtained in an acidic zinc sulfate electrolyte solution. Scanning electron microscopy（SEM）, X-ray diffraction（XRD）, and energy dispersive X-ray spectroscopy（EDXS） were used to observe the microstructural features of coating. Anodes of Al/conductive coating/α-PbO2-CeO2-TiO2/β-PbO2, Al/conductive coating/α-PbO2-CeO2-TiO2/β-PbO2-WC, Al/conductive coating/α-PbO2-CeO2-TiO2/β-PbO2-ZrO2, and Pb-1%Ag anodes were also researched. The results indicated that the Al/conductive coating/α-PbO2-CeO2-TiO2/β-PbO2-WC-ZrO2 showed the best catalytic activity and corrosion resistant performance; the intensity of diffraction peak exhibited the highest value as well as a new PbWO4 phase; the content of WC and ZrO2 in coating showed the highest value as well as the finest grain size.