Microstructure, Texture, and Hardness Evolutions of Al-Mg-Si-Cu Alloy during Annealing Treatment
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2019年第6期
论文作者：汪小锋 MA Cunqiang MA Pengcheng ZHOU Songze WANG Yonggang
文章页码：1288 - 1296
摘 要：Microstructure, texture and hardness evolutions of Al-Mg-Si-Cu alloy during annealing treatment were studied by microstructure, texture and hardness characterization in the present study. The experimental results show that microstructure, texture and hardness will change to some extent with the increase of annealing temperature. The microstructure transforms from the elongated bands to elongated grains first, and then the grains grow continuously. The texture transforms from the initial deformation texture b fiber to recrystallization texture mainly consisting of CubeND {001}<310> and P {011}<122> orientations first, and then the recrystallization texture may be enhanced continuously as a result of the grain growth. Hardness decreases slowly at first, and then decreases sharply and increases significantly finally. Besides, the particle distributions also have great changes. As the annealing temperature increases, they increase firstly as a result of precipitation, and then gradually disappear as a result of dissolution. Finally, the effect of annealing temperature on microstructure, texture and hardness evolutions is discussed.
汪小锋1，MA Cunqiang2，MA Pengcheng3，ZHOU Songze1，WANG Yonggang1
1. Key Laboratory of Impact and Safety Engineering (Ningbo University), Ministry of Education2. Capital Aerospace Machinery Company3. Aerospace Research Institute of Materials and Processing Technology
摘 要：Microstructure, texture and hardness evolutions of Al-Mg-Si-Cu alloy during annealing treatment were studied by microstructure, texture and hardness characterization in the present study. The experimental results show that microstructure, texture and hardness will change to some extent with the increase of annealing temperature. The microstructure transforms from the elongated bands to elongated grains first, and then the grains grow continuously. The texture transforms from the initial deformation texture b fiber to recrystallization texture mainly consisting of CubeND {001}<310> and P {011}<122> orientations first, and then the recrystallization texture may be enhanced continuously as a result of the grain growth. Hardness decreases slowly at first, and then decreases sharply and increases significantly finally. Besides, the particle distributions also have great changes. As the annealing temperature increases, they increase firstly as a result of precipitation, and then gradually disappear as a result of dissolution. Finally, the effect of annealing temperature on microstructure, texture and hardness evolutions is discussed.