Effect of cerium addition on oxidation behavior of 25Cr20Ni alloy under low oxygen partial pressure
来源期刊：JOURNAL OF RARE EARTHS2012年第2期
论文作者：邵明增 崔立山 郑雁军 邢琳琳
文章页码：164 - 169
摘 要：The influence of Ce addition on the oxidation behavior of 25Cr20Ni alloy at 950 oC under low oxygen partial pressure was inves-tigated. The oxidized samples were characterized by using X-ray diffraction （XRD）, scanning electron microscopy （SEM）, energy dispersive X-ray spectroscopy （EDS）, and scratch tester to obtain the oxide phases, morphology, thickness, composition and adhesion property of the oxide scales. The experiment results indicated that a small amount of Ce addition （0.02 wt.% or 0.05 wt.%） promoted oxidation resistance and inhibited the growth of the needlelike oxide. The Ce addition also decreased the formation of MnCr2O4 but promoted the SiO2 formation un-derneath the Cr2O3, which largely contributed to the improvement of oxide scale spallation resistance. For the sample with 0.3 wt.% Ce addi-tion, the oxidation rate significantly increased and the spallation resistance of the oxide scale decreased.
邵明增，崔立山，郑雁军，邢琳琳
Departments of Materials Science and Engineering, China University of Petroleum
摘 要：The influence of Ce addition on the oxidation behavior of 25Cr20Ni alloy at 950 oC under low oxygen partial pressure was inves-tigated. The oxidized samples were characterized by using X-ray diffraction （XRD）, scanning electron microscopy （SEM）, energy dispersive X-ray spectroscopy （EDS）, and scratch tester to obtain the oxide phases, morphology, thickness, composition and adhesion property of the oxide scales. The experiment results indicated that a small amount of Ce addition （0.02 wt.% or 0.05 wt.%） promoted oxidation resistance and inhibited the growth of the needlelike oxide. The Ce addition also decreased the formation of MnCr2O4 but promoted the SiO2 formation un-derneath the Cr2O3, which largely contributed to the improvement of oxide scale spallation resistance. For the sample with 0.3 wt.% Ce addi-tion, the oxidation rate significantly increased and the spallation resistance of the oxide scale decreased.
关键词：