Microstructure and magnetic properties of Nd-Fe-B sintered magnets with P addition

来源期刊：Rare Metals2019年第8期

论文作者：Fang Yang Guang-Le Dong Yan-Li Sui Si-Yang Ye Ping Li Cun-Guang Chen Xue-Xu Gao Zhi-Meng Guo

文章页码：770 - 775

摘要：In this paper,the effects of P doping on magnetic properties and microstructure were studied in Nd-Fe-B sintered magnets.With P doping,the grain size gets refined and the distribution of the main phase is optimized due to the reduction of the liquidus temperature.The liquidus temperature for the 0.05 wt% P-doped magnets is 1022 K,while that for the P-free magnets is 1038 K.As P content increases,the liquidus temperature significantly decreases.Clear and continuous grain boundary phases are formed in the P-containing magnets with smaller grain size.The optimized microstructure with average grain size of 8.43 μm is obtained in the 0.05 wt% P-doped magnets,which is approximately 0.69 μm smaller than that of P-free sintered magnets（9.12μm）.Though P is usually thought to be an impurity element,it might be beneficial in Nd-Fe-B sintered magnets with proper addition.The coercivity of the0.05 wt% P-doped magnets could be increased to1283 kA·m^-1,with slight changes of the remanence and the maximum magnetic energy product.NdP04 phases in the grain boundary are of hexagonal structure,while those at the triple junctions have monoclinic structure.Activated sintering is achieved by doping proper P element in the Nd-FeB sintered magnets.

稀有金属(英文版) 2019,38(08),770-775

Microstructure and magnetic properties of Nd-Fe-B sintered magnets with P addition

Fang Yang Guang-Le Dong Yan-Li Sui Si-Yang Ye Ping Li Cun-Guang Chen Xue-Xu Gao Zhi-Meng Guo

Institute of Advanced Materials and Technology,University of Science and Technology Beijing

Tianjian Sanhuan Lucky New Materials Inc.

State Key Laboratory for Advanced Metals and Materials,University of Science and Technology Beijing

作者简介：*Zhi-Meng Guo e-mail: zmguo@ustb.edu.cn;

收稿日期：2 May 2017

基金：financially supported by State Key Lab of Advanced Metals and Materials(No.2018-Z06);the Fundamental Research Funds for the Central Universities(No.FRFTP-18-025A1);

Microstructure and magnetic properties of Nd-Fe-B sintered magnets with P addition

Fang Yang Guang-Le Dong Yan-Li Sui Si-Yang Ye Ping Li Cun-Guang Chen Xue-Xu Gao Zhi-Meng Guo

Institute of Advanced Materials and Technology,University of Science and Technology Beijing

Tianjian Sanhuan Lucky New Materials Inc.

State Key Laboratory for Advanced Metals and Materials,University of Science and Technology Beijing

Abstract：

In this paper,the effects of P doping on magnetic properties and microstructure were studied in Nd-Fe-B sintered magnets.With P doping,the grain size gets refined and the distribution of the main phase is optimized due to the reduction of the liquidus temperature.The liquidus temperature for the 0.05 wt% P-doped magnets is 1022 K,while that for the P-free magnets is 1038 K.As P content increases,the liquidus temperature significantly decreases.Clear and continuous grain boundary phases are formed in the P-containing magnets with smaller grain size.The optimized microstructure with average grain size of 8.43 μm is obtained in the 0.05 wt% P-doped magnets,which is approximately 0.69 μm smaller than that of P-free sintered magnets(9.12μm).Though P is usually thought to be an impurity element,it might be beneficial in Nd-Fe-B sintered magnets with proper addition.The coercivity of the0.05 wt% P-doped magnets could be increased to1283 kA·m^-1,with slight changes of the remanence and the maximum magnetic energy product.NdP04 phases in the grain boundary are of hexagonal structure,while those at the triple junctions have monoclinic structure.Activated sintering is achieved by doping proper P element in the Nd-FeB sintered magnets.

Keyword：

Nd-Fe-B sintered magnets; P; Microstructure; Magnetic properties; Activated sintering;

Received： 2 May 2017

1 Introduction

In the last two decades,there has been a rapid growth in the permanent magnet electric motors and generators of (hybrid) vehicles industries [ 1, 2] .Nd-Fe-B sintered magnets have gained considerable attention due to their excellent magnetic properties of high maximum energy product and coercivity [ 3, 4, 5] .Typical Dy-free sintered Nd-Fe-B magnets with a coercive field (μ₀H_c) of～1.5 MA·m^-1 are sufficient for most room temperature applications [ 6, 7] .However,low Curie temperature and thermal stability limit their applications at high temperature above 473 K.At elevated temperatures,the effects of thermal activation on the reversal process increase,resulting in a significant reduction in coercivity [ 8, 9, 10] .Heavy rare earth elements such as Dy are commonly added to increase the coercivity in N d-Fe-B sintered magnets.Partial substitution of Dy for Nd in the 2:14:1 phase is known to form a (Nd,Dy)₂Fe₁₄B shell with higher magnetic anisotropy field at theouter region of the main phase grains [ 5, 11, 12, 13, 14] .However,there is a strong demand to achieve high coercivity without using Dy due to its scarcity and high cost.

It is well known that the magnetic properties can be improved by controlling the microstructure,especially addition of non-rare earth elements [ 15, 16, 17] .Numerous efforts have revealed that inhibiting grain growth,retaining grain boundaries and lowering melting point of Nd-rich phases are effective to increase the coercivity.Some researchers have reported that the addition of small amounts of Mo,W and Nb to Nd-Fe-B sintered magnets is effective in inhibiting grain growth [ 18, 19, 20, 21] .The grain boundaries of Nd-Fe-B sintered magnets were improved with addition of small amounts of Al,Ga or Cu [ 22, 23, 24] .On the other hand,it was reported that the fine-grained NdFe-B sintered magnets exhibit large coercivity (H^c) of1.85 T by the addition of low-C concentrations [ 25] .As we know,P is thought to be a harmful elelnent in most aspects of materials.Recently,Zhang et al. [ 26] found that a coercivity enhancement was obtained after the addition of P to Fe-Pt-B alloys.With P addition,the liquidus temperature of the alloy was lowered [ 27, 28] .However,little is known about the effect of P addition on the micro structure and magnetic properties of Nd-Fe-B sintered magnets.The research about P introduction in the magnets was rarelyreported.

In this study,the effect of small amount of P on microstructure and magnetic properties of Nd-Fe-B magnets was investigated.In addition,the mechanism of grain refinement with P introduction in the magnets was established.The magnetic and microstructural properties of P-doped magnets were compared with those of P-free magnets.

2 Experimental

2.1 Materials preparation

The commercial Nd-Fe-B and P powders were used as the raw materials.The purity of the raw materials was over99%.Nd-Fe-B powders (～5μm) with a nominal composition of 31.0Re(Re-Nd,Pr)-0.5Dy-bal.Fe-1.0B-4.0 M(wt%,M-Cu,Al,Co,Cr,Ga) were mixed with various amounts of commercially available P (0 wt%,0.05 wt%,0.10 wt%,0.20 wt%) powders.This was performed by ball milling for 2 h using SPEX-8000 mixer/mill with a steel ball-to-powder weight ratio of 5:1.The average particle size of P powder was about 5μm.After being pressed in a magnetic field of 1352 kA·m^-1,the green compacts were vacuum-sintered at 1323 K for 3 h.Subsequently,the magnets were annealed at 1203 K for 3 h following subsequent annealing at 758 K for 6 h.

2.2 Microstructural and properties characterization

The magnets were cut into cylinder shape with a dimensional size ofΦ8 mm×5 mm by wire electrode cutting.Four samples of each P content were conducted to confirm reproducibility.Densities of the sintered magnets were determined by Archimedes’principle measurement.The room temperature magnetic properties of the processed magnets bymechanical polishing were measured by a magnetic measurement device NIM-200C(National Institute of Metrology,PR China).The characterization of the samples by differential scanning calorimetry (DSC,NETZSCHSTA449) was performed using 200-mg crushed sintered magnets in an alumina box under protective Ar gas.Microstructural studies were conducted by backscattered scanning electron microscope (SEM,Supra55)equipped with an energy-dispersive spectroscopy detector(EDS),using monochromatic Cu Kαradiation with the wavelength of X-ray0.154 nm and operated at 40 kV as well as 150 mA.Elemental distribution was performed using electron probe microanalysis (EPMA,JEOL,JXA-8230) operated at 0.2-30.0 kV as well as 1×10^-12-1×10^-5 A.Phase composition and identification were operated by transmission electron microscope (TEM,JEM2010) combined with energy-dispersive spectroscopy detector (EDS) and selected area electron diffraction(SAED).Thin foil specimens for TEM analysis were prepared using an ion milling system.

3 Results and discussion

3.1 Magnetic properties

All sintered Nd-Fe-B magnets were crack-free.The densities of the magnets are above 7.5 g·cm^-3,as shown in Table 1.With the increase in P content,the density of the Nd-Fe-B sintered magnets decreases.The density for the0.20 wt%P-doped magnets decreases from 7.59 to7.52 g·cm^-3.

Table 1 also shows the magnetic properties of the P-containing magnets as a function of P content.The measured coercivity (H_c),remanence (B_r) and maximum magnetic energy product ((BH)_max) of the undoped magnets are 1236 kA-m^-1,1.230 T and 292.2 kJ·m^-3,respectively.Compared with the undoped magnets,the coercivity for the 0.05 wt%P-doped magnet increases from 1236 to 1283 kA·m^-1 and the peak value is 3.8%higher than that of P-free magnets.In addition,there is no noticeable changes in B_r and (BH)_max.Proper P addition is beneficial to improve the coercivity in Nd-Fc-B sintered magnets.Upon further increasing P content,the magnetic properties significantly decrease.With 0.10 wt%P addition,the coercivity decreases from 1283 to 1254 kA-m^-1.The introduction of 0.20 wt%P results in obvious decrease in coercivity and remanence.The coercivity decreases to1206 kA·m^-1,and the peak value is 6.0%lower than that of 0.05 wt%P-doped magnet,as shown in Table 1.And the corresponding B_r decreases from 1.227 to 1.219 T.Also,(BH)_max decreases from 290.9 to 287.5 kJ·m^-3.Figure 1 compares corresponding demagnetization curves of P-free and P-doped magnets.It is obvious that the coercivity gets enhanced when P content is not more than0.10 wt%.Excessive P introduction leads to a deterioration in density and magnetic performance.

下载原图

Table 1 Magnetic properties of P-doped Nd-Fe-B magnets as functions of P content

Fig.1 Demagnetization curves for P-doped Nd-Fe-B sintered magnets

The introduction of P in P-doped magnets may cause the changes of grain size distribution or change the structure of grain boundaries.To understand the effects of P doping on microstructure and magnetic performance in magnets,DSC,FESEM,EPMA and TEM investigations were conducted.

3.2 DSC curves

Figure 2 shows DSC curves of Nd-Fe-B sintered magnets as a function of P content.DSC analysis was performed from room temperature to 1323 K at a constant heating rate of 0.67 K·s^-1.Two endothermic peaks are observed on all DSC curves.The first temperature,T_x1,corresponds to Curie temperature of Nd₂Fe₁₄B phase,while the second endothermic peak,T_x2,corresponds to the melting point of Nd-rich eutectic phases.Compared with P-free magnets,T_x1 remains about the same in P-containing magnets.And the first temperature T_x1 is close to 600 K.In the undoped magnets,the second temperature,T_x2,is 1038 K.When P content is 0.05 wt%,temperature decreases to 1022 K.The second temperature decreases to 1013 K with 0.20 wt%P,as shown in Fig.2.The second temperature decreases with P content increasing.During sintering,Nd-rich eutectic phases precipitate in a liquid form at T_x2.It suggests that the liquidus temperature is lowered with P addition.P doping reduces the melting point and increases the fluidity of the liquid Nd-rich phase during sintering.

Fig.2 DSC curves of Nd-Fe-B sintered magnets with P addition(x=0 wt%-0.20 wt%)

3.3 Microstructures

Figure 3 shows the microstructure changes and grain size distribution in the magnets with different P contents.Figure 3a shows typical microstructure of the sintered magnets,in which the dark gray corresponds to Nd₂Fe₁₄B matrix phase and the bright regions are various Nd-rich intergranular phases.The Nd-rich grain boundary phases(GBPs) are unclear and discontinuous between two ferromagnetic Nd₂Fe₁₄B phase grains.Besides,the 2:14:1 phase grains are not uniform and the grain size is relatively large.With P doping,distributions of GBPs and the main phase grain size are optimized,as shown in Fig.3b.Compared with P-free magnets,clear and continuous GBPs are formed in P-doped magnets,which is beneficial to diminish the magnetic exchange interactions between neighboring grains and enhance the magnetic isolations.

In P-free magnets,the average grain size is 9.12μm.The grain size is relatively small,and the grain size distribution is more uniform in P-doped magnets,as shown in Fig.3e,f.The average grain size of 0.05 wt%P-doped magnets decreases to 8.43μm,which is approximately0.69μm less than that of P-free magnets.When P content increases to 0.20 wt%,the average grain size reduces to7.88μm.But there exist obvious defects,as shown in Fig.3c,which may work against the magnetic performance.It can be indicated that the grain growth gets inhibited with P addition.Additionally,Nd₂Fe₁₄B phase grains become rounder and more uniform,indicating that the wettability between the main phase and the intergranular phase gets improved.As a result,in the 0.05 wt%P-doped magnets,the coercivity gets enhanced with the remanence slightly changing.Excessive P introduction leads to the deterioration of the magnetic properties.Probably,the reduction of the magnetic properties occurs due to the decrease in the density and the content of the main phase.It can be inferred that proper P introduction promotes the uniformity and continuity of GBPs because the melting point decreases during sintering [ 29] .

Fig.3 SEM images and grain size distribution of magnets with different P contents:a,d 0 wt%;b,e 0.05 wt%;c,f 0.20 wt%

3.4 Phase distribution and composition

Figure 4 shows the distribution of Nd,O and P in the undoped and 0.05 wt%P-doped magnets.It can be observed that Nd is dominant in the intergranular phases and O is also enriched in the phases.Both Nd and O are the essential components of Nd-rich phase at the triple junctions.NdO_x oxides are the main form of Nd-rich phases.The distribution of P in the P-containing magnets is not uniform.P is enriched in Nd-rich phases,just like the white mark shown in Fig.4b.It can be inferred that P-containing precipitates may be phosphorus oxide phases.

To further characterize elemental distribution,the spatial distribution of Fe,P,Nd and O across the main phase and intergranular phase was measured by EDS line-scan.Figure 5b-e shows the composition variation across the region.P is clearly enriched in Nd-rich phases.The distribution of P is not uniform,and obvious clustering is observed.There are no P-precipitates in the main phases.In P-rich phases,there exist Nd,O and P.It can be inferred that the potential form of P-rich phase might be NdO_xP_yphase.

Fig.4 SEM images and EPMA mapping images of Nd,O and P elements of magnets with different P contents:a 0 wt%and b 0.05 wt%

Fig.5 High-magnification backscattered SEM images and EDS patterns in 0.05 wt%P-doped magnets:a SEM images and line-scan profiles for b P,c Nd,d Fe and e O indexed as red arrow in a

Fig.6 TEM images and SAED patterns of a NdPO₄ phase in GBPs,b NdPO₄ phase at triple junctions,and c EDS results of areas A-C in0.05 wt%P-doped magnets

Figure 6 presents TEM images and EDS results of the phosphorus oxide phases in 0.05 wt%P-doped magnets.Particularly interesting is the observation that P-rich phase is found to simultaneously exist in the grain boundary and in the triple junctions.Corresponding SAED patterns show that P-precipitates are NdPO₄ phases.NdPO₄ phase in the grain boundary is identified as hexagonal structure with lattice parameters of a=0.698 nm,b=0.698 nm and c=0.634 nm,as shown in Fig.6a.But,the grain size of NdPO₄ phase is large.In addition,SAED patterns of NdPO₄ phase at the triple junctions are matching to the monoclinic structure,with lattice parameters of a=0.674 nm,b=0.696 nm and c=0.641 nm.EDS results also confirm that NdPO₄ phase tends to precipitate in different regions.

4 Conclusion

In summary,the effects of P doing on magnetic properties and microstructure in Nd-Fe-B sintered magnets were investigated.The melting point of Nd-rich eutectic phase is lowered with P content increasing,leading to the wettability improvement and grain growth inhibition.In0.05 wt%P-doped magnets,the melting point decreases from 1038 to 1022 K.And,the average grain size and grain size distribution are optimized,with forming clear and continuous GBPs.As a result,the magnets with 0.05 wt%P addition show a larger coercivity of 1283 kA·m^-1,without notable changes in remanence and the maximum magnetic energy product,as compared to that of the undoped magnets.In the P-containing magnets,NdPO₄phases mainly are precipitated in the grain boundary and triple junctions.Though P acts as a harmful element in most aspects of materials,it is beneficial for activating sintering with proper addition in Nd-Fe-B sintered magnets.

Acknowledgements This study was financially supported by State Key Lab of Advanced Metals and Materials (No.2018-Z06) and the Fundamental Research Funds for the Central Universities (No.FRF-TP-18-025A1).