Accelerated flow softening and dynamic transformation of Ti-6Al-4V alloy in two-phase region during hot deformation via coarsening αgrain
来源期刊:JOURNAL OF MATERIALS SCIENCE TECHNOLOG2020年第1期
论文作者:Xiankun Ji Baoqi Guo Fulin Jiang Hong Yu Dingfa Fu Jie Teng Hui Zhang John J.Jonas
文章页码:160 - 166
摘 要:The flow softening is an important phenomenon during hot deformation of metallic materials.In the present work,a more evident flow softening of Ti-6 Al-4 V alloy when deformed in two-phase region was observed in coarser a grain sample,which was attributed to an accelerated dynamic transformation from harder α phase into β phases.Notably,full β microstructure was observed in coarse grain samples at strain of 1.2,while retained a phase was observed in fine a grain specimens.In the views of thermodynamics and crystallographic analysis,the in-depth mechanisms of dynamic transformation were further investigated.
Xiankun Ji1,2,Baoqi Guo2,Fulin Jiang1,Hong Yu1,Dingfa Fu1,Jie Teng1,Hui Zhang1,John J.Jonas2
1. College of Materials Science and Engineering, Hunan University2. Materials Engineering, McGill University
摘 要:The flow softening is an important phenomenon during hot deformation of metallic materials.In the present work,a more evident flow softening of Ti-6 Al-4 V alloy when deformed in two-phase region was observed in coarser a grain sample,which was attributed to an accelerated dynamic transformation from harder α phase into β phases.Notably,full β microstructure was observed in coarse grain samples at strain of 1.2,while retained a phase was observed in fine a grain specimens.In the views of thermodynamics and crystallographic analysis,the in-depth mechanisms of dynamic transformation were further investigated.