Microstructure and microwave dielectric properties of Ba6-3xSm8+2xTi18O54 ceramics with various BaxSr1-xTiO3 additions
来源期刊:Journal of Rare Earths2012年第2期
论文作者:周玲玲 周洪庆 邵辉 朱海奎
文章页码:142 - 145
摘 要:The Ba6-3xSm8+2xTi18O54 (x=2/3) microwave dielectric ceramics were prepared by traditional solid sate reaction technique. The ex-periment was based on the Ba6-3xSm8+2xTi18O54 (BST) microwave dielectric ceramics doped with a certain amount of Bi2O3, then the effects of BaxSr1-xTiO3 additives on the structure and microwave dielectric properties of Ba6-3xSm8+2xTi18O54 ceramics were investigated using X-ray diffraction and scanning electron microscopy. In this study, the small amount substitution of Sr for Ba was effective for the microwave dielec-tric properties of BST, especially the τf could be tuned to near zero. The result showed that the BST possessed excellent dielectric properties when the addition of Bi2O3 and BaxSr1-xTiO3 was 1 wt.% respectively: εr=79.6, Q?f=10789 GHz, τf=-1.5 ppm/oC.
周玲玲,周洪庆,邵辉,朱海奎
College of Materials Science and Engineering, Nanjing University of Technology
摘 要:The Ba6-3xSm8+2xTi18O54 (x=2/3) microwave dielectric ceramics were prepared by traditional solid sate reaction technique. The ex-periment was based on the Ba6-3xSm8+2xTi18O54 (BST) microwave dielectric ceramics doped with a certain amount of Bi2O3, then the effects of BaxSr1-xTiO3 additives on the structure and microwave dielectric properties of Ba6-3xSm8+2xTi18O54 ceramics were investigated using X-ray diffraction and scanning electron microscopy. In this study, the small amount substitution of Sr for Ba was effective for the microwave dielec-tric properties of BST, especially the τf could be tuned to near zero. The result showed that the BST possessed excellent dielectric properties when the addition of Bi2O3 and BaxSr1-xTiO3 was 1 wt.% respectively: εr=79.6, Q?f=10789 GHz, τf=-1.5 ppm/oC.
关键词: