Low-cycle fatigue lifetime estimation of Ti–6Al–4V welded joints by a continuum damage mechanics model
来源期刊：Rare Metals2016年第4期
论文作者：Hong-Yu Qi Xiao-Lei Zheng Xiao-Guang Yang
文章页码：299 - 302
摘 要：The low-cycle fatigue（LCF）behavior of directionally solidified nickel-based superalloy Ti–6Al–4V was studied under bare and electron beam welding conditions at room temperature.Results show that:（1）under the same test conditions,all the joints exhibit lower LCF lifetime than Ti–6Al–4V;（2）the failure of welded structures is mainly ascribed to the welding defect.A novel lifetime prediction methodology based on continuum damage mechanics is proposed to predict the lifetime of Ti–6Al–4V and its welded joints.
摘要：The low-cycle fatigue（LCF）behavior of directionally solidified nickel-based superalloy Ti–6Al–4V was studied under bare and electron beam welding conditions at room temperature.Results show that:（1）under the same test conditions,all the joints exhibit lower LCF lifetime than Ti–6Al–4V;（2）the failure of welded structures is mainly ascribed to the welding defect.A novel lifetime prediction methodology based on continuum damage mechanics is proposed to predict the lifetime of Ti–6Al–4V and its welded joints.
关键词：