Preparation and Characterization of Three-dimensional Chrysanthemun Flower-like Calcium Carbonate
来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2012年第4期
论文作者:陈先勇
文章页码:708 - 714
摘 要:Calcium carbonate with three-dimensional chrysanthemun flower-like structure was successfully prepared from calcium chloride and sodium carbonate ethanol/water mixed solution by a simple precipitation method,using trisodium citrate as crystal modifier.The experimental results show that the three-dimensional structure of chrysanthemun flower-like calcium carbonate is built up with several symmetrical micrometer multi-layer petals arranged around the multi-layer pancake-liked center,and the micrometer center and petals are assemblied by a large number of nanometer spherical particles with size 10-20 nm.It is found that the amount of trisodium citrate,the ethanol volume content has an important influence on the formation of this morphology.A possible mechanism is proposed to explain the formation of three-dimensional chrysanthemun flower-like calcium carbonate according the results.Scanning electron microscopy(SEM),X-ray powder diffraction(XRD),flourier transform infrared spectroscopy(FT-IR),thermogravimety analysis(TG),transmission electron microscopy(TEM) equipped with energy-dispersive X-ray(EDX),and selected area electron diffraction(SAED) were used to characterize the crystals.
陈先勇
Institute of Chemical Engineering,Sichuan UniversityCollege of Chemical and Environmental Engnineering,Hubei University for Nationalities
摘 要:Calcium carbonate with three-dimensional chrysanthemun flower-like structure was successfully prepared from calcium chloride and sodium carbonate ethanol/water mixed solution by a simple precipitation method,using trisodium citrate as crystal modifier.The experimental results show that the three-dimensional structure of chrysanthemun flower-like calcium carbonate is built up with several symmetrical micrometer multi-layer petals arranged around the multi-layer pancake-liked center,and the micrometer center and petals are assemblied by a large number of nanometer spherical particles with size 10-20 nm.It is found that the amount of trisodium citrate,the ethanol volume content has an important influence on the formation of this morphology.A possible mechanism is proposed to explain the formation of three-dimensional chrysanthemun flower-like calcium carbonate according the results.Scanning electron microscopy(SEM),X-ray powder diffraction(XRD),flourier transform infrared spectroscopy(FT-IR),thermogravimety analysis(TG),transmission electron microscopy(TEM) equipped with energy-dispersive X-ray(EDX),and selected area electron diffraction(SAED) were used to characterize the crystals.
关键词: