Synthesis of Polycrystalline Yb:Gd3Ga5O12 Nanopowders by Homogeneous Precipitation Method
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2010年第1期
论文作者：黄德馨 刘景和
文章页码：123 - 126
摘 要：The Ytterbium doped gadolinium gallium garnet [Yb3+:Gd3Ga5O12, Yb:GGG] precursor powders were synthesized via homogeneous precipitation method using Yb2O3, Ga2O3, Gd2O3 and ammonium bicarbonate [NH4HCO3] as precipitator, and ammonium sulfate [（NH4）2SO4] as additive. The evolution of phase composition and micro-structure of the powders were characterized by TG- DTA, XRD, IR, and TEM. The results indicate that all precursor powders completely transform to Yb:GGG phase by calcining at 900 ℃ for 8 h, the resultant powders are well dispersed and have smaller particle size approximately 80 nm owing to the electrostatic effect.
黄德馨1,2，刘景和1
1. Department of Materials Science and Engineering,Changchun University of Science and Technology2. Department of Materials Science and Engineering,Jilin Architectural and Civil Engineering Institute
摘 要：The Ytterbium doped gadolinium gallium garnet [Yb3+:Gd3Ga5O12, Yb:GGG] precursor powders were synthesized via homogeneous precipitation method using Yb2O3, Ga2O3, Gd2O3 and ammonium bicarbonate [NH4HCO3] as precipitator, and ammonium sulfate [（NH4）2SO4] as additive. The evolution of phase composition and micro-structure of the powders were characterized by TG- DTA, XRD, IR, and TEM. The results indicate that all precursor powders completely transform to Yb:GGG phase by calcining at 900 ℃ for 8 h, the resultant powders are well dispersed and have smaller particle size approximately 80 nm owing to the electrostatic effect.
关键词：