Effects of Deformation Modes on Texture Evolution during Hot Working of Al-Zn-Mg-Cu-Zr Alloy
来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2016年第3期
论文作者:赵晓东 LU Ruilong LIN Jinbao 陈慧琴
文章页码:616 - 623
摘 要:Deformation modes have strong effects on deformation textures and subsequent annealing textures during hot working of metals. Micro-textures and macro-textures during hot axisymmetric and planar compressive deformation and subsequent annealing processes of Al-Zn-Mg-Cu-Zr alloy were investigated by EBSD and XRD respectively. The EBSD testing indicated that for the axisymmetric compressive deformation, Brass along the α-fiber and Goss present in the sample deformed at 350 ℃, Rotated-Cube was present and Brass transformed to Goss along α-fiber after annealing; Rotated-Cube appeared only in the deformation at 420 ℃, which decreased and Brass appeared after annealing. For the planar compressive deformation, Rotated-Cube and Brass aligned to α and β fibers present in the deformation at 350 ℃, Rotated-Cube texture transformed to Brass along the α-fiber after annealing; Rotated-Cube and Brass were present in the deformation at 420 ℃, and the Rotated-Cube was enhanced and Brass transformed to Goss after annealing. Shearing textures dominated on the surface of the specimen. XRD testing showed that Rotated-Cube and a few Goss dominated in the thickplates formed by upsetting and drawing, which transformed to Cube after annealing; However, Brass and Cube textures present in the thick-plates formed by rolling besides Rotated-Cube and Goss textures, which remained in the plates after annealing.
赵晓东1,LU Ruilong2,LIN Jinbao3,陈慧琴1
1. School of Materials Science and Engineering, Taiyuan University of Science and Technology2. School of Materials Science and Engineering, University of Science and Technology Beijing3. School of Applied Science,Taiyuan University of Science and Technology
摘 要:Deformation modes have strong effects on deformation textures and subsequent annealing textures during hot working of metals. Micro-textures and macro-textures during hot axisymmetric and planar compressive deformation and subsequent annealing processes of Al-Zn-Mg-Cu-Zr alloy were investigated by EBSD and XRD respectively. The EBSD testing indicated that for the axisymmetric compressive deformation, Brass along the α-fiber and Goss present in the sample deformed at 350 ℃, Rotated-Cube was present and Brass transformed to Goss along α-fiber after annealing; Rotated-Cube appeared only in the deformation at 420 ℃, which decreased and Brass appeared after annealing. For the planar compressive deformation, Rotated-Cube and Brass aligned to α and β fibers present in the deformation at 350 ℃, Rotated-Cube texture transformed to Brass along the α-fiber after annealing; Rotated-Cube and Brass were present in the deformation at 420 ℃, and the Rotated-Cube was enhanced and Brass transformed to Goss after annealing. Shearing textures dominated on the surface of the specimen. XRD testing showed that Rotated-Cube and a few Goss dominated in the thickplates formed by upsetting and drawing, which transformed to Cube after annealing; However, Brass and Cube textures present in the thick-plates formed by rolling besides Rotated-Cube and Goss textures, which remained in the plates after annealing.
关键词: