Characteristics of TIG arc-assisted laser welding–brazing joint of aluminum to galvanized steel with preset filler powder

来源期刊:Rare Metals2015年第9期

论文作者:Chun-Ling Li Ding Fan Bin Wang

文章页码:650 - 656

摘    要:Tungsten inert gas(TIG) arc-assisted laser welding–brazing was used for the butt joining of 5A06 aluminum alloy to the galvanized steel by preset filler powder without groove. The spreading behavior of liquid metal on the back of the galvanized steel at different assisted welding currents was also investigated. The results show that the assisted TIG arc optimizes the interface reaction temperature, enhances the wettability of liquid metal on the steel side, and forms a sound butt joint at an appropriate welding current. A non-uniform intermetallic compound is formed at the interfacial layer, which is composed of Fe2Al5 close to the steel substrate and Fe4Al13 close to the solidified aluminum. The superior tensile strength of joint is indicated when the welding current ranges from 13 to 16 A. The average tensile strength can reach 151 MPa at the welding current of 16 A, and the corresponding fracture belongs to the ductile and brittle hybrid mode.

详情信息展示

Characteristics of TIG arc-assisted laser welding–brazing joint of aluminum to galvanized steel with preset filler powder

摘要:Tungsten inert gas(TIG) arc-assisted laser welding–brazing was used for the butt joining of 5A06 aluminum alloy to the galvanized steel by preset filler powder without groove. The spreading behavior of liquid metal on the back of the galvanized steel at different assisted welding currents was also investigated. The results show that the assisted TIG arc optimizes the interface reaction temperature, enhances the wettability of liquid metal on the steel side, and forms a sound butt joint at an appropriate welding current. A non-uniform intermetallic compound is formed at the interfacial layer, which is composed of Fe2Al5 close to the steel substrate and Fe4Al13 close to the solidified aluminum. The superior tensile strength of joint is indicated when the welding current ranges from 13 to 16 A. The average tensile strength can reach 151 MPa at the welding current of 16 A, and the corresponding fracture belongs to the ductile and brittle hybrid mode.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号