工艺参数对爆炸喷涂WC-Co涂层性能均匀性的影响
来源期刊:金属学报2011年第1期
论文作者:王铁钢 宋丙红 华伟刚 宫骏 孙超
文章页码:115 - 122
关键词:爆炸喷涂; WC-Co涂层; 孔隙率; 显微硬度; 弹性模量; 微尺度磨粒磨损
Key words:detonation gun spraying; WC-Co coating; porosity; microhardness; elastic modulus; micro-scale abrasive wear
摘 要:采用正交实验,分别研究了氧燃率、喷涂距离对爆炸喷涂WC-Co涂层性能的影响.通过工艺优化,获得了结构均匀致密、硬度高、弹性模量大、耐磨性能好的WC-Co涂层.利用XRD和SEM分析涂层的物相组成、观察其微观结构,经截面与表面力学性能和磨损性能对比,优化后的涂层表现出近似各向同性特征.分析指出涂层均匀的微观结构及低孔隙率是导致其近似各向同性特征的主要原因.
Abstract: Based on the orthogonal experiment, the effects of oxygen-fuel ratio and spraying distance on physical and mechanical properties of D-gun sprayed WC-Co coatings were investigated. An ideal coating with the uniform dense microstructures, high hardness and elastic modulus, and excellent wear resistance was obtained by technology optimization. The phase identifications and microstructure observation of the optimized WC-Co coating were conducted by XRD and SEM, respectively. The coating showed near-isotropic behaviors, which has been verified by the comparisons of mechanical and wear properties between cross section and surface. The mechanisms how the spraying parameters affected near-isotropic characters of the D-gun sprayed WC-Co coating were analyzed and discussed.
王铁钢1,宋丙红2,华伟刚1,宫骏2,孙超2
(1.辽宁省沈阳市科学院金属研究所金属腐蚀与防护国家重点实验室
2.中航工业哈尔滨东安发动机(集团)有限公司,哈尔滨 150066)
摘 要:采用正交实验,分别研究了氧燃率、喷涂距离对爆炸喷涂WC-Co涂层性能的影响.通过工艺优化,获得了结构均匀致密、硬度高、弹性模量大、耐磨性能好的WC-Co涂层.利用XRD和SEM分析涂层的物相组成、观察其微观结构,经截面与表面力学性能和磨损性能对比,优化后的涂层表现出近似各向同性特征.分析指出涂层均匀的微观结构及低孔隙率是导致其近似各向同性特征的主要原因.
关键词:爆炸喷涂; WC-Co涂层; 孔隙率; 显微硬度; 弹性模量; 微尺度磨粒磨损