Effect of Rare Earths on Structure and Properties of Carbonitriding Boronizing Combined Treatment
来源期刊：Journal of Rare Earths2007年第S1期
论文作者：叶宏 闫忠琳 田中青
文章页码：415 - 418
摘 要：The microstructure, thickness, microhardness and wear resistance of single-boronizing, carbonitriding+boronizing and carbonitriding+RE-boronizing layers of 16Mn steel were investigated respectively. Effect of rare earths on microstructure and properties of the penetrated layer were studied and the mechanism of effects of rare earths was discussed. The result showed that the structure, microhardness, brittleness and wear resistance of the penetrated layer after carbonitriding+ RE-boronizing were better than that of conventional boronizing and carbonitriding, especially the wear resistance of boronized layer was increased remarkably. The RE-boronizing layer of the steel is single phase Fe2B, and RE elements enhanced Fe2B （002） direction texture. The distribution of rare earth element （La） in the layer was non-uniform. RE content is higher between borides than that of the interior of borides. An optimum value of the addition of RE element in the agent was 8%. The average service life of the 16Mn steel brick mould treated by carbonitriding+RE-boronizing was 1.5 times as long as the service life of the mould treated by carbonitriding-boronizing.
叶宏，闫忠琳，田中青
摘 要：The microstructure, thickness, microhardness and wear resistance of single-boronizing, carbonitriding+boronizing and carbonitriding+RE-boronizing layers of 16Mn steel were investigated respectively. Effect of rare earths on microstructure and properties of the penetrated layer were studied and the mechanism of effects of rare earths was discussed. The result showed that the structure, microhardness, brittleness and wear resistance of the penetrated layer after carbonitriding+ RE-boronizing were better than that of conventional boronizing and carbonitriding, especially the wear resistance of boronized layer was increased remarkably. The RE-boronizing layer of the steel is single phase Fe2B, and RE elements enhanced Fe2B （002） direction texture. The distribution of rare earth element （La） in the layer was non-uniform. RE content is higher between borides than that of the interior of borides. An optimum value of the addition of RE element in the agent was 8%. The average service life of the 16Mn steel brick mould treated by carbonitriding+RE-boronizing was 1.5 times as long as the service life of the mould treated by carbonitriding-boronizing.
关键词：