Size dependence of up-conversion luminescence of NaYF4:Yb3+/Tm3+
来源期刊:JOURNAL OF RARE EARTHS2010年第S1期
论文作者:刘晓戈 代如成 王中平 张增明
文章页码:215 - 218
摘 要:Tm3+/Yb3+ codoped NaYF4 microcrystals were synthesized using a hydrothermal method.The bright upconversion light was observed under 980 nm excitation.The upconversion luminescence was systematically investigated at different Yb3+ concentrations and different reaction temperatures and time.The sample with 60% Yb3+ concentration and reacting at 180 oC for 24 h possessed the highest luminescent efficiency.The higher luminescent efficiency was contributed to a large surface area.The large surface area induced the large vibration mode by absorbed H2O and CO2.The larger vibration mode could enhance the energy transfer efficiency from the excited Yb3+ to Tm3+ by the process of phonon assisted energy transfer.
刘晓戈1,代如成1,王中平2,张增明2
1. Department of Physics,University of Science and Technology of China2. The Centre of Physical Experiments,University of Science and Technology of China
摘 要:Tm3+/Yb3+ codoped NaYF4 microcrystals were synthesized using a hydrothermal method.The bright upconversion light was observed under 980 nm excitation.The upconversion luminescence was systematically investigated at different Yb3+ concentrations and different reaction temperatures and time.The sample with 60% Yb3+ concentration and reacting at 180 oC for 24 h possessed the highest luminescent efficiency.The higher luminescent efficiency was contributed to a large surface area.The large surface area induced the large vibration mode by absorbed H2O and CO2.The larger vibration mode could enhance the energy transfer efficiency from the excited Yb3+ to Tm3+ by the process of phonon assisted energy transfer.
关键词: