Preparation and Thermal Stability of Phosphate System Protection Glasses Doped with Rare Earths
来源期刊:Journal of Rare Earths2006年第S1期
论文作者:孟献丰
文章页码:211 - 214
摘 要:<正>The formation ability and thermal stability of phosphate laser protection glass doped with high Sm2O3 content were discussed. The characteristic temperatures ( Tg, Tc, Tm) were measured by DSC and the crystallization parameter β was calculated. The results show that the forming regions would shrink and tend to closed ellipse with increasing of Sm2O3 content. Increasing of BaO/Al2O3 ratio changes the network structure of rare earth glass and improves the thermal stability finally. However, with the increasing of Sm2O3 content, the β increases firstly and then decreases, and finally the thermal stability also increases firstly and then decreases.
孟献丰1
1. School of Material Science and Engineering,Jiangsu University
摘 要:<正>The formation ability and thermal stability of phosphate laser protection glass doped with high Sm2O3 content were discussed. The characteristic temperatures ( Tg, Tc, Tm) were measured by DSC and the crystallization parameter β was calculated. The results show that the forming regions would shrink and tend to closed ellipse with increasing of Sm2O3 content. Increasing of BaO/Al2O3 ratio changes the network structure of rare earth glass and improves the thermal stability finally. However, with the increasing of Sm2O3 content, the β increases firstly and then decreases, and finally the thermal stability also increases firstly and then decreases.
关键词: