Thermal stability and optical properties of a novel Tm3+ doped fluorotellurite glass
来源期刊：Journal of Rare Earths2014年第12期
论文作者：成茵 吴钟晴 胡茜 吴腾宴 周伟伟
文章页码：1154 - 1161
摘 要：A series of fluorotellurite glasses based on（81–x）Te O2-（10+x）KF-9La2O3（TKL）, where x=0 mol.%, 5 mol.%, 10 mol.%, 15 mol.%, doped with 2000 ppm Tm2O3, were prepared by the conventional melt quenching method.The influence of KF content on the thermal stability and optical spectroscopic properties of the Tm3+ doped fluorotellurite glasses were investigated by differential scanning calorimetry（DSC）, X-ray diffraction（XRD）, density measurement, Fourier transform infrared spectroscopy（FTIR）, UV-VIS-NIR optical spectroscopy and fluorescence spectroscopy.Judd-Ofelt intensity parameters of Tm3+ in as-prepared glasses were determined and used to calculate the spontaneous emission probabilities and the radiative lifetime for the 4f-4f transitions of the Tm3+ ions.Stimulated emission cross sections in the 1470 nm region（σse） were evaluated by Füchtbauer-Ladenburg formula.The results showed that KF substitution of Te O2 was beneficial to improving the thermal stability, decreasing glass density and reducing the content of OH related groups for the investigated fluorotellurite glasses.The glass with composition of 66 Te O2-25KF-9La2O3（named TKL25） had the longest radiative lifetime of the 3H4（361 μs） and the largest FWHM×σse value（420.07×10–28 cm3）, which made it a promising material for S-band fiber amplifiers.
成茵，吴钟晴，胡茜，吴腾宴，周伟伟
College of Physics and Electronic Science, Changsha University of Science & Technology
摘 要：A series of fluorotellurite glasses based on（81–x）Te O2-（10+x）KF-9La2O3（TKL）, where x=0 mol.%, 5 mol.%, 10 mol.%, 15 mol.%, doped with 2000 ppm Tm2O3, were prepared by the conventional melt quenching method.The influence of KF content on the thermal stability and optical spectroscopic properties of the Tm3+ doped fluorotellurite glasses were investigated by differential scanning calorimetry（DSC）, X-ray diffraction（XRD）, density measurement, Fourier transform infrared spectroscopy（FTIR）, UV-VIS-NIR optical spectroscopy and fluorescence spectroscopy.Judd-Ofelt intensity parameters of Tm3+ in as-prepared glasses were determined and used to calculate the spontaneous emission probabilities and the radiative lifetime for the 4f-4f transitions of the Tm3+ ions.Stimulated emission cross sections in the 1470 nm region（σse） were evaluated by Füchtbauer-Ladenburg formula.The results showed that KF substitution of Te O2 was beneficial to improving the thermal stability, decreasing glass density and reducing the content of OH related groups for the investigated fluorotellurite glasses.The glass with composition of 66 Te O2-25KF-9La2O3（named TKL25） had the longest radiative lifetime of the 3H4（361 μs） and the largest FWHM×σse value（420.07×10–28 cm3）, which made it a promising material for S-band fiber amplifiers.
关键词：