Optimizing the microstructures and mechanical properties of Al-Cu-based alloys with large solidification intervals by coupling travelling magnetic fields with sequential solidification
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG2021年第2期
论文作者：Lei Luo Liangshun Luo Robert O.Ritchie Yanqing Su Binbin Wang Liang Wang Ruirun Chen Jingjie Guo Hengzhi Fu
文章页码：100 - 113
摘 要：Alloys with large solidification intervals are prone to issues from the disordered growth and defect formation; accordingly, finding ways to effectively optimize the microstructure, further to improve the mechanical properties is of great importance. To this end, we couple travelling magnetic fields with sequential solidification to continuously regulate the mushy zones of Al-Cu-based alloys with large solidification intervals. Moreover, we combine experiments with simulations to comprehensively analyze the mechanisms on the optimization of microstructure and properties. Our results indicate that only downward travelling magnetic fields coupled with sequential solidification can obtain the refined and uniform microstructure, and promote the growth of matrix phase -Al along the direction of temperature gradient.Additionally, the secondary dendrites and precipitates are reduced, while the solute partition coefficient and solute solid-solubility are raised. Ultimately, downward travelling magnetic fields can increase the ultimate tensile strength, yield strength, elongation and hardness from 196.2 MPa, 101.2 MPa, 14.5 % and85.1 kg mm-2 without travelling magnetic fields to 224.1 MPa, 114.5 MPa, 17.1 % and 102.1 kg mm-2,and improve the ductility of alloys. However, upward travelling magnetic fields have the adverse effects on microstructural evolution, and lead to a reduction in the performance and ductility. Our findings demonstrate that long-range directional circular flows generated by travelling magnetic fields directionally alter the transformation and redistribution of solutes and temperature, which finally influences the solidification behavior and performance. Overall, our research present not only an innovative method to optimize the microstructures and mechanical properties for alloys with large solidification intervals,but also a detailed mechanism of travelling magnetic fields on this optimization during the sequential solidification.
Lei Luo1，Liangshun Luo1，Robert O.Ritchie2，Yanqing Su1，Binbin Wang1，Liang Wang1，Ruirun Chen1，Jingjie Guo1，Hengzhi Fu1
1. National Key Laboratory for Precision Hot Processing of Metals, School of Materials Science & Engineering, Harbin Institute of Technology2. Department of Materials Science and Engineering, University of California
摘 要：Alloys with large solidification intervals are prone to issues from the disordered growth and defect formation; accordingly, finding ways to effectively optimize the microstructure, further to improve the mechanical properties is of great importance. To this end, we couple travelling magnetic fields with sequential solidification to continuously regulate the mushy zones of Al-Cu-based alloys with large solidification intervals. Moreover, we combine experiments with simulations to comprehensively analyze the mechanisms on the optimization of microstructure and properties. Our results indicate that only downward travelling magnetic fields coupled with sequential solidification can obtain the refined and uniform microstructure, and promote the growth of matrix phase -Al along the direction of temperature gradient.Additionally, the secondary dendrites and precipitates are reduced, while the solute partition coefficient and solute solid-solubility are raised. Ultimately, downward travelling magnetic fields can increase the ultimate tensile strength, yield strength, elongation and hardness from 196.2 MPa, 101.2 MPa, 14.5 % and85.1 kg mm-2 without travelling magnetic fields to 224.1 MPa, 114.5 MPa, 17.1 % and 102.1 kg mm-2,and improve the ductility of alloys. However, upward travelling magnetic fields have the adverse effects on microstructural evolution, and lead to a reduction in the performance and ductility. Our findings demonstrate that long-range directional circular flows generated by travelling magnetic fields directionally alter the transformation and redistribution of solutes and temperature, which finally influences the solidification behavior and performance. Overall, our research present not only an innovative method to optimize the microstructures and mechanical properties for alloys with large solidification intervals,but also a detailed mechanism of travelling magnetic fields on this optimization during the sequential solidification.
关键词：