Luminescent polymer electrolytes based on chitosan and containing europium triflate
来源期刊：JOURNAL OF RARE EARTHS2016年第7期
论文作者：R.Alves A.S.S.de Camargo A.Pawlicka M.M.Silva
文章页码：661 - 666
摘 要：Solid polymer electrolytes based on chitosan and europium triflate were prepared by solvent casting and characterized by X-ray diffraction, scanning electron microscopy（SEM）, atomic force microscopy（AFM）, and photoluminescence spectroscopy. The X-ray diffraction exhibited that the samples were essentially amorphous with organized regions over the whole range of the salt content studied. The AFM analysis demonstrated that the smoother sample had roughness of 4.39 nm. Surface visualization through SEM revealed good homogeneity without any phase separation for more conductive samples and the less conductive showed some imperfections on the surface. The emission and excitation spectra displayed the characteristic bands of Eu（CF3SO3）3 in addition to broad bands corresponding to the polymer host. The excited state 5D0 lifetime values ranged from 0.29–0.37 ms for the studied samples.
R.Alves1，A.S.S.de Camargo2，A.Pawlicka3，M.M.Silva4
1. Center of Chemistry,University of Minho2. S?o Carlos Institute of Physics,University of Sao Paulo3. S?o Carlos Institute of Chemistry, University of Sao Paulo4. Center of Chemistry, University of Minho
摘 要：Solid polymer electrolytes based on chitosan and europium triflate were prepared by solvent casting and characterized by X-ray diffraction, scanning electron microscopy（SEM）, atomic force microscopy（AFM）, and photoluminescence spectroscopy. The X-ray diffraction exhibited that the samples were essentially amorphous with organized regions over the whole range of the salt content studied. The AFM analysis demonstrated that the smoother sample had roughness of 4.39 nm. Surface visualization through SEM revealed good homogeneity without any phase separation for more conductive samples and the less conductive showed some imperfections on the surface. The emission and excitation spectra displayed the characteristic bands of Eu（CF3SO3）3 in addition to broad bands corresponding to the polymer host. The excited state 5D0 lifetime values ranged from 0.29–0.37 ms for the studied samples.
关键词：