Reduction and melting behavior of carbon composite lateritic bauxite pellets
来源期刊:International Journal of Minerals Metallurgy and Materials2015年第4期
论文作者:Ying-yi Zhang Jie Zhao Yuan-hong Qi Xiang-li Cheng Zong-shu Zou
文章页码:381 - 388
摘 要:Direct reduction of low-grade lateritic bauxite was studied at high temperature to recover Fe and beneficiate Al2O3 slag. The results show that a metallization rate of 97.9% and a nugget recovery rate of 85.1% can be achieved when the reducing and melting temperatures are 1350 and 1480°C, respectively. Moreover, a higher-grade calcium aluminate slag(Al2O3 = 50.52wt%) can also be obtained, which is mainly composed of α-Al2O3, hercynite(Fe Al2O4), and gehlenite(Ca2Al2SiO7). In addition, high-quality iron nuggets have been produced from low-grade lateritic bauxite. The nugget is mainly composed of iron(93.82wt%) and carbon(3.86wt%), with almost no gangue(slag).
Ying-yi Zhang1,2,Jie Zhao1,Yuan-hong Qi1,Xiang-li Cheng1,Zong-shu Zou2
1. State Key Laboratory of Advance Steel Processes and Products, Central Iron and Steel Research Institute2. School of Material and Metallurgy, Northeast University
摘 要:Direct reduction of low-grade lateritic bauxite was studied at high temperature to recover Fe and beneficiate Al2O3 slag. The results show that a metallization rate of 97.9% and a nugget recovery rate of 85.1% can be achieved when the reducing and melting temperatures are 1350 and 1480°C, respectively. Moreover, a higher-grade calcium aluminate slag(Al2O3 = 50.52wt%) can also be obtained, which is mainly composed of α-Al2O3, hercynite(Fe Al2O4), and gehlenite(Ca2Al2SiO7). In addition, high-quality iron nuggets have been produced from low-grade lateritic bauxite. The nugget is mainly composed of iron(93.82wt%) and carbon(3.86wt%), with almost no gangue(slag).