Quantitative Characterization and Elastic Properties of Interfacial Transition Zone around Coarse Aggregate in Concrete
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2017年第4期
论文作者：刘须收 HAN Yunge 张亚梅 QIU Chen HU Chuanlin LI Zongjin
文章页码：838 - 844
摘 要：Backscattered electron images（BSE） obtained by scanning electron microscope was used to quantitatively characterize the microstructure of interfacial transition zone（ITZ） in concrete. Influences of aggregate size（5, 10, 20, and 30 mm）, water to cement ratio（0.23, 0.35 and 0.53） and curing time（from 3d to 90d） on the microstructure of interfacial transition zone between coarse aggregate and bulk cement matrix were investigated. The volume percentage of detectable porosity and unhydrated cement in ITZ was quantitatively analyzed and compared with that in the matrix of various concretes. Nanoindentation technology was applied to obtain the elastic properties of ITZ and matrix, and the elastic modulus of concrete was then calculated based on the Lu & Torquato model and self-consistence scheme by using the ITZ thickness and elastic modulus obtained from this investigation. The experimental results demonstrated that the microstructure and thickness of ITZ in concrete vary with a variety of factors, like aggregate size, water to cement ratio and curing time. The relative low elastic properties of ITZ should be paid attention to, especially for early age concrete.
贾子健1，HAN Yunge1，张亚梅1，QIU Chen1，HU Chuanlin2，LI Zongjin2
1. School of Materials Science and Engineering, Jiangsu Key Laboratory of Construction Materials, Southeast University2. Department of Civil and Environmental Engineering, The Hong Kong University of Science and Technology
摘 要：Backscattered electron images（BSE） obtained by scanning electron microscope was used to quantitatively characterize the microstructure of interfacial transition zone（ITZ） in concrete. Influences of aggregate size（5, 10, 20, and 30 mm）, water to cement ratio（0.23, 0.35 and 0.53） and curing time（from 3d to 90d） on the microstructure of interfacial transition zone between coarse aggregate and bulk cement matrix were investigated. The volume percentage of detectable porosity and unhydrated cement in ITZ was quantitatively analyzed and compared with that in the matrix of various concretes. Nanoindentation technology was applied to obtain the elastic properties of ITZ and matrix, and the elastic modulus of concrete was then calculated based on the Lu & Torquato model and self-consistence scheme by using the ITZ thickness and elastic modulus obtained from this investigation. The experimental results demonstrated that the microstructure and thickness of ITZ in concrete vary with a variety of factors, like aggregate size, water to cement ratio and curing time. The relative low elastic properties of ITZ should be paid attention to, especially for early age concrete.
关键词：