Sintering and Phase Transformation of 7wt% Calcia-stabilized Zirconia Ceramics

来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2009年第2期

论文作者:陈常连

文章页码:304 - 307

摘    要:Calcia stabilized zirconia(CSZ) ceramics were prepared with 7wt% calcia-stabilized zirconia powder by pressureless sintering technology. The crystal phases of the sintered samples were studied by X-ray diffraction(XRD) and Raman spectroscopy techniques, and the microstructures of the fracture surfaces were observed by scanning electron spectroscopy(SEM). The phase compositions and the lattice parameters of cubic calcia-stabilized zirconia were calculated by XRD patterns. As the sintering temperature increasing from 1400 ℃ to 1600 ℃, the monoclinic zirconia content decreases gradually, finally all monoclinic phase transforms to cubic calcia-stabilized zirconia, which is determined to be Ca0.134Zr0.866O1.866. It is revealed that monoclinic zirconia is the main factor causing minute cracks on the surface of sintered samples, and the combination of the XRD patterns and Raman spectra is an effective way to research the phase transformations of zirconia.

详情信息展示

Sintering and Phase Transformation of 7wt% Calcia-stabilized Zirconia Ceramics

陈常连

State Key Lab of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology

摘 要:Calcia stabilized zirconia(CSZ) ceramics were prepared with 7wt% calcia-stabilized zirconia powder by pressureless sintering technology. The crystal phases of the sintered samples were studied by X-ray diffraction(XRD) and Raman spectroscopy techniques, and the microstructures of the fracture surfaces were observed by scanning electron spectroscopy(SEM). The phase compositions and the lattice parameters of cubic calcia-stabilized zirconia were calculated by XRD patterns. As the sintering temperature increasing from 1400 ℃ to 1600 ℃, the monoclinic zirconia content decreases gradually, finally all monoclinic phase transforms to cubic calcia-stabilized zirconia, which is determined to be Ca0.134Zr0.866O1.866. It is revealed that monoclinic zirconia is the main factor causing minute cracks on the surface of sintered samples, and the combination of the XRD patterns and Raman spectra is an effective way to research the phase transformations of zirconia.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号