Synthesis and Characterization of Mg3（PO4）2-coated Li1.05Ni1/3Mn1/3Co1/3O2 Cathode Material for Li-ion Battery
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2009年第3期
论文作者：陈玉红
文章页码：347 - 353
摘 要：Mg3（PO4）2-coated Li1.05Ni1/3Mn1/3Co1/3O2 cathode materials were synthesized via co-precipitation method. The morphology, structure, electrochemical performance and thermal stability were characterized by scanning electron microscopy （SEM）, X-ray diffraction （XRD）, cyclic voltammetry（CV）, electrochemical impedance spectroscopy（EIS）, charge/discharge cycling and differential scanning calorimeter （DSC）. SEM analysis shows that Mg3（PO4）2-coating changes the morphologies of their particles and increases the grains size. XRD and CV results show that Mg3（PO4）2-coating powder is homogeneous and has better layered structure than the bare one. Mg3（PO4）2-coating improved high rate discharge capacity and cycle-life performance. The reason why the cycling performance of Mg3（PO4）2-coated sample at 55 ℃ was better than that of room temperature was the increasing of lithium-ion diffusion rate and charge transfer rate with temperature rising. Mg3（PO4）2-coating improved the cathode thermal stability, and the result was consistent with thermal abuse tests using Li-ion cells: the Mg3（PO4）2 coated Li1.05Ni1/3Mn1/3Co1/3O2 cathode did not exhibit thermal runaway with smoke and explosion, in contrast to the cells containing the bare Li1.05Ni1/3Mn1/3Co1/3O2.
陈玉红
Department of Chemical and Environmental Engineering, Hebei Chemical & Pharmaceutical Vocational Technology Colege
摘 要：Mg3（PO4）2-coated Li1.05Ni1/3Mn1/3Co1/3O2 cathode materials were synthesized via co-precipitation method. The morphology, structure, electrochemical performance and thermal stability were characterized by scanning electron microscopy （SEM）, X-ray diffraction （XRD）, cyclic voltammetry（CV）, electrochemical impedance spectroscopy（EIS）, charge/discharge cycling and differential scanning calorimeter （DSC）. SEM analysis shows that Mg3（PO4）2-coating changes the morphologies of their particles and increases the grains size. XRD and CV results show that Mg3（PO4）2-coating powder is homogeneous and has better layered structure than the bare one. Mg3（PO4）2-coating improved high rate discharge capacity and cycle-life performance. The reason why the cycling performance of Mg3（PO4）2-coated sample at 55 ℃ was better than that of room temperature was the increasing of lithium-ion diffusion rate and charge transfer rate with temperature rising. Mg3（PO4）2-coating improved the cathode thermal stability, and the result was consistent with thermal abuse tests using Li-ion cells: the Mg3（PO4）2 coated Li1.05Ni1/3Mn1/3Co1/3O2 cathode did not exhibit thermal runaway with smoke and explosion, in contrast to the cells containing the bare Li1.05Ni1/3Mn1/3Co1/3O2.
关键词：