Experimental observation of solidification of undercooled single phase alloys

来源期刊:中国有色金属学报(英文版)2000年第6期

论文作者:李金富 杨根仓 张雪萍 周尧和

文章页码:705 - 708

Key words:undercooled alloy; solidification; high speed cinematography; microstructure evolution

Abstract: The solidification process of undercooled Cu70Ni30 alloy melt in a cylindrical crucible was investigated by high speed cinematography. In the experiment, nucleation location was controlled at one end of the sample by means of artificial triggering. The results show that the equiaxed dendritic crystals obtained at low undercooling form in sequential solidification, rather than simultaneously in the entire sample, and the morphology of the recalescence front frequently changes with time. If increment of undercooling results in that the dendrite growth is controlled by thermal diffusion, the primary dendrite arms propagate parallel to each other in〈100〉, and eventually directional solidification microstructure is obtained. At higher undercooling, dendrite growth is destabilized due to solidification contraction, and the microstructure develops into fine quasi-spherical grains through recrystallization, however, the massive nucleation is not found.

详情信息展示

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号