Effect of La2O3 content on wear resistance of alumina ceramics
来源期刊：Journal of Rare Earths2016年第3期
论文作者：吴婷婷 周建 吴伯麟 李文杰
文章页码：288 - 294
摘 要：In order to improve the wear resistance, a kind of alumina ceramic with good wear resistance was created in an Al2O3-CaCO3-SiO2-MgO-La2O3（ACSML） system. The effects of La2O3 content on sintering temperature, bulk density, and wear rate were investigated. The wear rate of sample was as low as 0.0393‰. The wear resistance of the sample containing La2O3 has improved 43% than that of the sample without La2O3. Appropriate La2O3 doping could inhibit grain growth, enhance density, and purify grain boundary. La2O3 could diffuse into Al2O3 to form a solid solution and react with Al2O3 to form high-aluminum low-lanthanum complex oxides. The combination among Al2O3, the solid solution layer, and the layer of high-aluminum low-lanthanum complex oxides combined closely, which could improve grain boundary cohesion. Besides, the homogeneous distributions of elements made uniform structure. Finally, the wear resistance of alumina ceramic was improved.
吴婷婷1，周建1，吴伯麟2，李文杰2
1. State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology2. College of Materials Science and Engineering, Guilin University of Technology
摘 要：In order to improve the wear resistance, a kind of alumina ceramic with good wear resistance was created in an Al2O3-CaCO3-SiO2-MgO-La2O3（ACSML） system. The effects of La2O3 content on sintering temperature, bulk density, and wear rate were investigated. The wear rate of sample was as low as 0.0393‰. The wear resistance of the sample containing La2O3 has improved 43% than that of the sample without La2O3. Appropriate La2O3 doping could inhibit grain growth, enhance density, and purify grain boundary. La2O3 could diffuse into Al2O3 to form a solid solution and react with Al2O3 to form high-aluminum low-lanthanum complex oxides. The combination among Al2O3, the solid solution layer, and the layer of high-aluminum low-lanthanum complex oxides combined closely, which could improve grain boundary cohesion. Besides, the homogeneous distributions of elements made uniform structure. Finally, the wear resistance of alumina ceramic was improved.
关键词：