Preparation of AZ91D Slurries for Semi-Solid Forming Using Al8 ( Mn, Fe) 5 Precipitates
来源期刊：JOURNAL OF RARE EARTHS2004年增刊第2期
论文作者：Heon Phil Ha Jeong Man Doh Ji Young Byun Soon Il Kwon
Key words：AZ91D alloy; semi-solid forming; solidification; heterogeneous nucleation;
Abstract: During the solidification of the AZ91D-alloys, the Al8(Mn, Fe)5 phase is generally precipitated in the melt in advance of the precipitation of the primary α-Mg. The basic principle for manufacturing AZ91D-alloy slurries for semi solid forming is to use the Al8(Mn, Fe)5 precipitates as the heterogeneous nucleation sites for primary α-Mg phases. Microscopic analysis for the location of the Al8(Mn, Fe)5 precipitate explains that the Al8(Mn, Fe)5 precipitate is the effective heterogeneous nucleation site for the primary α-Mg phase. It was also observed that increase of the Mn content in the melt and the cooling rate below to the solid/liquid two-phase region resulted in smaller and more globular primary α-Mg due to the increase of heterogeneous nucleation sites. It was found that the average α-Mg diameter grew as a function of t0.278, where t is the holding time at the solid/liquid two-phase region. This would be attributed to the Ostwald type ripening and coalescence between primary α-Mg phases. The cooling rate below to the solid/liquid two-phase region, Mn content in AZ91D alloy, and the holding time and temperature affected on the quality of slurry.
Heon Phil Ha1，Jeong Man Doh1，Ji Young Byun1，Soon Il Kwon1
(1.Metal Processing Research Center,Division of Materials,Korea Institute of Science and Technology,# 39-1 Haweolgok-Dong,Sungbuk-Ku,Seoul 136-791,Republic of Korea)
Abstract:During the solidification of the AZ91D-alloys, the Al8(Mn, Fe)5 phase is generally precipitated in the melt in advance of the precipitation of the primary α-Mg. The basic principle for manufacturing AZ91D-alloy slurries for semi solid forming is to use the Al8(Mn, Fe)5 precipitates as the heterogeneous nucleation sites for primary α-Mg phases. Microscopic analysis for the location of the Al8(Mn, Fe)5 precipitate explains that the Al8(Mn, Fe)5 precipitate is the effective heterogeneous nucleation site for the primary α-Mg phase. It was also observed that increase of the Mn content in the melt and the cooling rate below to the solid/liquid two-phase region resulted in smaller and more globular primary α-Mg due to the increase of heterogeneous nucleation sites. It was found that the average α-Mg diameter grew as a function of t0.278, where t is the holding time at the solid/liquid two-phase region. This would be attributed to the Ostwald type ripening and coalescence between primary α-Mg phases. The cooling rate below to the solid/liquid two-phase region, Mn content in AZ91D alloy, and the holding time and temperature affected on the quality of slurry.
Key words:AZ91D alloy; semi-solid forming; solidification; heterogeneous nucleation;