Influence of heat treatment regimes on microstructures and fracture characteristics of 7055Al alloy containing Ag

来源期刊：中国有色金属学报(英文版)2004年第3期

论文作者：李海 郑子樵 王芝秀

文章页码：505 - 509

Key words：7055Al alloy; heat treatment; fracture characteristic; intergranular cracking; transgranular cracking

Abstract: Tensile properties, fracture characteristics and microstructures of 7055 aluminum-based alloy containing Ag after T6, T73 and RRA treatment were investigated. The results show that RRA treatment retains strength of 7055-T6 with higher electrical conductivity close to that of 7055-T73 alloy, but its elongation decreases greatly. SEM fractographs reveal that intergranular cracking and shear-type transgranular cracking are both presented on the fracture appearance of 7055-T6 specimen. After T73 treatment, the fractographs mainly consist of dimple-type transgranular cracking with minor intergranular cracking. For 7055-RRAspecimen, intergranular cracking dominates with minor dimples on the fracture surface. The type and size of precipitates, width of grain boundary and the ability of precipitates to impede dislocation motion vary with heat treatment regimes. Three frature models were built on the basis of microstructural analyses.