Corrosion behavior of rare earth cerium based conversion coating on aluminum alloy
来源期刊:Journal of Rare Earths2010年第S1期
论文作者:赵丹 孙杰 张丽丽 谭勇 李季
文章页码:371 - 374
摘 要:The present paper focused on the use of the salt of rare earth cerium as corrosion inhibitor of aluminum by using cathodic electrolytic passivation method.The corrosion resistance and the microphology of the cerium passivation film were studied by the methods of electrochemical method,scanning electron microscopy(SEM),and energy dispersive spectroscopic analysis.From the results,it was shown that good corrosion resistance of cerium-based passive coating was obtained when the compositions were as follows:CeCl3·7H2O,0.05 mol/L;H2O2,30 ml/L;current density,1.1 mA/cm2;temperature,40 oC;time,9 min.SEM and EDS revealed that the cerium conversion coatings formed on the surface of aluminum alloy were related to cerium hydroxide/hydrated oxide depositions.
赵丹,孙杰,张丽丽,谭勇,李季
School of Environmental and Chemical Engineering,Shenyang Ligong University
摘 要:The present paper focused on the use of the salt of rare earth cerium as corrosion inhibitor of aluminum by using cathodic electrolytic passivation method.The corrosion resistance and the microphology of the cerium passivation film were studied by the methods of electrochemical method,scanning electron microscopy(SEM),and energy dispersive spectroscopic analysis.From the results,it was shown that good corrosion resistance of cerium-based passive coating was obtained when the compositions were as follows:CeCl3·7H2O,0.05 mol/L;H2O2,30 ml/L;current density,1.1 mA/cm2;temperature,40 oC;time,9 min.SEM and EDS revealed that the cerium conversion coatings formed on the surface of aluminum alloy were related to cerium hydroxide/hydrated oxide depositions.
关键词: