Effect of Rolling Process on Comprehensive Properties of Corrosion Resistant Steel for Bottom Plate of Cargo Oil Tanks
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2016年第2期
论文作者：于驰 王平 GAO Xiuhua DU Linxiu
文章页码：379 - 386
摘 要：A new kind of corrosion resistant steelfor cargo oiltanks（COT）was developed.The influences of finalrolling temperature,cooling rate,and finalcooling temperature on microstructure were investigated.The proper rolling process parameters were obtained through multi-pass thermalsimulation test.The finalrolling temperature is about 820 ℃,the finalcooling temperature is about 600 ℃,and the cooling rate should be controlled between 10 ℃/s and 20 ℃/s.Based on the above analysis of the results,three groups of rolling samples by thermo mechanicalcontrolprocess are prepared.The tensile strength,yield strength,and toughness of the corrosion resistant steelare measured,which meet the requirements of DH36 steel,it can instruct the actualrolling production.The corrosion behaviour is also researched by weight loss and electrochemicalimpedance spectroscopic method,and it is found that the steelhas good corrosion resistance performance,the best one is No.3 steel,the corrosion rate of which is about 1/4 of the accepted criterion.
于驰1，王平1，GAO Xiuhua2，DU Linxiu2
1. Key Laboratory of National Education Ministry for Electromagnetic Processing of Materials,Northeastern University2. The State Key Laboratory of Rolling and Automation,Northeastern University
摘 要：A new kind of corrosion resistant steelfor cargo oiltanks（COT）was developed.The influences of finalrolling temperature,cooling rate,and finalcooling temperature on microstructure were investigated.The proper rolling process parameters were obtained through multi-pass thermalsimulation test.The finalrolling temperature is about 820 ℃,the finalcooling temperature is about 600 ℃,and the cooling rate should be controlled between 10 ℃/s and 20 ℃/s.Based on the above analysis of the results,three groups of rolling samples by thermo mechanicalcontrolprocess are prepared.The tensile strength,yield strength,and toughness of the corrosion resistant steelare measured,which meet the requirements of DH36 steel,it can instruct the actualrolling production.The corrosion behaviour is also researched by weight loss and electrochemicalimpedance spectroscopic method,and it is found that the steelhas good corrosion resistance performance,the best one is No.3 steel,the corrosion rate of which is about 1/4 of the accepted criterion.
关键词：