PRECIPITATION BEHAVIOR OF M2N IN A HIGH-NITROGEN AUSTENITIC STAINLESS STEEL DURING ISOTHERMAL AGING
来源期刊：Acta Metallurgica Sinica2007年第2期
论文作者：F. Shi W.F. Cui L.J. Wang C.M. Liu
Key words：austenitic stainless steel; high nitrogen; microstructure; isothermal aging; precipitation;
Abstract: The precipitation behavior of M2N and the microstructural evolution in a Cr-Mn austenitic stainless steel with a high nitrogen content of 0.43mass% during isothermal aging has been investigated using optical microscopy (OM), scanning electron microscopy ( SEM), and transmission electron microscopy (TEM). The aging treatments have led to the decomposition of nitrogen supersaturated austenitic matrix through discontinuous cellular precipitation. The precipitated cells comprise alternate lamellae of M2N precipitate and austenitic matrix. This kind of precipitate morphology is similar to that of pearlite. However, owing to the non-eutectoidic mechanism of the reaction, the growth characteristic of the cellular precipitates is different from that of pearlite in Fe-C binary alloys. M2N precipitate in the cell possesses a hexagonal crystal structure with the parameters a=0.4752nm and c=0.4429nm, and the orientation relationship between the MN precipitates and austenite determined from the SADP is [01110]M2N// [101]γ,[2-1-10]M2N// [010]γ.
F. Shi1，W.F. Cui1，L.J. Wang1，C.M. Liu1
(1.School of Materials & Metallurgy, Northeastern University,Shenyang 110004, China)
Abstract:The precipitation behavior of M2N and the microstructural evolution in a Cr-Mn austenitic stainless steel with a high nitrogen content of 0.43mass% during isothermal aging has been investigated using optical microscopy (OM), scanning electron microscopy ( SEM), and transmission electron microscopy (TEM). The aging treatments have led to the decomposition of nitrogen supersaturated austenitic matrix through discontinuous cellular precipitation. The precipitated cells comprise alternate lamellae of M2N precipitate and austenitic matrix. This kind of precipitate morphology is similar to that of pearlite. However, owing to the non-eutectoidic mechanism of the reaction, the growth characteristic of the cellular precipitates is different from that of pearlite in Fe-C binary alloys. M2N precipitate in the cell possesses a hexagonal crystal structure with the parameters a=0.4752nm and c=0.4429nm, and the orientation relationship between the MN precipitates and austenite determined from the SADP is [01110]M2N// [101]γ,[2-1-10]M2N// [010]γ.
Key words:austenitic stainless steel; high nitrogen; microstructure; isothermal aging; precipitation;