Growth, structural, thermal properties and spectroscopic characteristics of KTb（WO4）2 single crystal
来源期刊：Journal of Rare Earths2012年第10期
论文作者：李静 王继扬 韩树娟 郭永解 王永政
文章页码：967 - 971
摘 要：KTb（WO4）2（KTW） single crystal with dimensions up to 30mm×30mm×10mm was grown by the top-seeded solution growth （TSSG） method for the first time. The crystal structure was refined at room temperature by using single crystal X-ray diffraction data. Absorption and fluorescence spectra were measured at room temperature. The fluorescence lifetime of KTb（WO4）2 was 114μs. The specific heat of the KTb（WO4）2 crystal was also measured at room temperature.
李静，王继扬，韩树娟，郭永解，王永政
State Key Laboratory of Crystal Materials, Shandong University
摘 要：KTb（WO4）2（KTW） single crystal with dimensions up to 30mm×30mm×10mm was grown by the top-seeded solution growth （TSSG） method for the first time. The crystal structure was refined at room temperature by using single crystal X-ray diffraction data. Absorption and fluorescence spectra were measured at room temperature. The fluorescence lifetime of KTb（WO4）2 was 114μs. The specific heat of the KTb（WO4）2 crystal was also measured at room temperature.
关键词：