Durability of Alite-calcium Barium Sulphoaluminate Cement
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2009年第6期
论文作者：芦令超
文章页码：982 - 985
摘 要：The durability of the cement was mainly studied. Under 1.0 MPa of hydraulic pressure for 8 hours, water could penetrate completely through the sample made by portland cement, but could not penetrate through that by alite-barium sulphoaluminate cement. Under the condition of freezing and thawing cycle, the loss ratio of compressive strength of the cement was only about 17.3% at curing 28 d ages, but the loss of portland cement was as high as 29.5%. Alite-calcium barium sulphoaluminate cement also has an excellent resistance to sulfate attack. The coefficients of resistance to sulfate attack of the cement exceeded 1.0. Meanwhile, the composition and microstructure of the hardened paste of alite-calcium barium sulphoaluminate cement were analyzed by XRD and SEM.
芦令超
School of Materials Science and Engineering,University of Jinan
摘 要：The durability of the cement was mainly studied. Under 1.0 MPa of hydraulic pressure for 8 hours, water could penetrate completely through the sample made by portland cement, but could not penetrate through that by alite-barium sulphoaluminate cement. Under the condition of freezing and thawing cycle, the loss ratio of compressive strength of the cement was only about 17.3% at curing 28 d ages, but the loss of portland cement was as high as 29.5%. Alite-calcium barium sulphoaluminate cement also has an excellent resistance to sulfate attack. The coefficients of resistance to sulfate attack of the cement exceeded 1.0. Meanwhile, the composition and microstructure of the hardened paste of alite-calcium barium sulphoaluminate cement were analyzed by XRD and SEM.
关键词：