稀有金属(英文版) 2018,37(09),743-749

Electrochemical property of LiFePO₄/C composite cathode with different carbon sources

Xin Li Yu Zhi Jiang Xi Kun Li Hai Xia Jiang Jun Long Liu Jun Feng Shi Bin Lin Xin Guan

Shenyang Ligong University

作者简介：*Xi Kun Li,e-mail:kunxi@163.com;

收稿日期：16 July 2015

基金：financially supported by the National Natural Science Foundation of China (No.51274143);

Electrochemical property of LiFePO₄/C composite cathode with different carbon sources

Xin Li Yu Zhi Jiang Xi Kun Li Hai Xia Jiang Jun Long Liu Jun Feng Shi Bin Lin Xin Guan

Shenyang Ligong University

Abstract：

To improve the performance of battery cathode materials that consist of carbonaceous organic material,carbon coatings on lithium iron phosphate (LiFePO₄/C)materials were synthesized by different carbon sources.LiFePO₄/C was synthesized by a combination method of sol-gel and gas-phase diffused permeation. LiFeO₄/C materials were prepared by coating different carbon contents. High-performance composite materials were prepared by combining carbon with element doped by two modified methods. The elements of Fe and C came from Fe3+and sucrose, glucose, citric acid. Thermogravimetrydifferential thermal analysis (TG-DTA), X-ray diffractometer (XRD), scanning electron microscope (SEM),cycle voltammetry (CV), and charge-discharge test were used to characterize and test the surface morphology,structure, and electrochemical performance. The results show that LiFePO₄/C synthesized with sucrose has higher specific discharge capacity than the other materials. The specific discharge capacity of this material is 84.27 mAh·g^-1. The capacity retention could attain 94%of the initial discharge capacity after 30 cycles, showing good electrochemical performance.

Keyword：

Solgel; Gas-phase diffused permeation; LiFePO₄/C; Sucrose; Citric acid;

Received： 16 July 2015

1 Introduction

Since LiFePO₄ was reported [ 1] ,it has received much attention and research.Compared with similar cathode materials such as LiCoO₂ which is short of resources,expensive,and toxic,as an interesting cathode material for lithium ion batteries,LiFePO₄ cathode materials have advantages of excellent thermal stability,low cost,nontoxic,friendly to environment,etc.It becomes one of the most potential cathode materials for its high theoretical capacity which is up to 170 mAh·g^-1 [ 1, 2, 3, 4] .LiFePO₄/C is olivine-structured,orthorhombic,and its space group is orthorhombic system (Pnma [ 5] ).The way to prepare LiFePO₄ is solid-phase method [ 6, 7] ,liquid-phase method [ 8, 9, 10] ,and microwave synthesis [ 11] .Its structural features make it have good cycle stability,but prevent the diffusion and electronic motion of lithium ion [ 12] ,leading to low electronic conductivity and diffusion rate of lithium ion.In order to improve the diffusion rate of lithium ion and the electronic conductivity of cathode material,most of the research is mainly carried out by coating the conductive material,doping ion,and decreasing particle size to improve the electrochemical properties of materials [ 13] .

The solid-phase method is limited for the uneven phase,irregular crystals,large sizes,long period,and so on.Coating the surface of LiFePO₄ can improve the conductivity among the particles and reduce the particle size to achieve the purpose of improving the electrochemical performance of LiFePO₄.S tudies have shown that coating the carbon surface can improve the high current discharge performance of the samples [ 14, 15] .Therefore,the LiFePO₄ was modified by coating method [ 16] ,during which solid-phase coating [ 17] and gel coating [ 18] were taken.

Gas-phase diffusion permeation method originates from multi-component rare earth infiltration method which is the technology based on the basic standpoint of physical chemistry,using special structural characteristics and chemical properties of rare earth elements to modify metal surface.The earliest multi-element rare earth penetration method focused on rare earth permeating treatment [ 19] of pure 20 Steel and 08 Steel surfaces.In recent years,multicomponent rare earth infiltration method has expanded to the polyoxometalates diffusion,processing many new functional materials.Based on the results of multi-element rare earth penetration [ 20] ,carbon coating was combined with gas-phase diffusion.Dispersive carbon was used as an electronic transport pathway to improve the electrical conductivity and the electrochemical performance.Through preparation of carbon-coated LiFePC₄/C,it was aimed to enhance the conductivity of the material,increase the surface area of the material,and make the material and the electrolyte contact fully to improve the internal particle removal/block performance of Li⁺and significantly improve the charge and discharge capacity as well as cycle performance [ 21, 22] of the material.

2 Experimental

2.1 Reagents and instruments

Ferric nitrate (Fe(NO₃)3·9H₂O)(analytically pure),lithium nitrate (LiNO₃)(analytically pure),mono-ammonium phosphate[MAP](NH₄H₂PO₄)(analytically pure),sucrose(analytically pure),glucose (analytically pure),citric acid(analytically pure),and methanol (analytically pure) were purchased from Sinopharm Chemical Reagent Ltd.,and lithium tablets (Beijing Research Institute of Nonferrous Metals),acetylene black (Shanghai Haotian Chemical Co.,Ltd.),and polyvinylidene fluoride PVDF (industrial grade,Shanghai Hersbit Chemical Co.Ltd.) were also purchased.

S ample gas-phase diffusion experiment was carried out in gas-phase diffusion furnace (XMT-101).High-temperature thermal gravimetric (TG,ZRY-2P,Shanghai Precision and Scientific Instrument Co.Ltd.) analyzer and high temperature difference thermal analyzer (DTA,CRY-2P) were used to confirm the vapor diffusion temperature of the material;X-ray diffractometer (XRD,D/max-2000,Japan Science Company) was used to do the material phase analysis;scanning electron microscope (SEM,S-4800,Japan Hitachi company) was used to analyze surface topography of the material;battery assembly was carried out in the STX-type vacuum glove box;charge and discharge tests were completed in highly accurate test system of battery performance(BTS-5 V/2 mA,Shenzhen Xinweier Electronic Co.Ltd.)and electrochemical workstation (CHI 604C,Shanghai Chenhua Company);data acquisition and process were completed by Xinwei data processing software.

2.2 Experimental process

2.2.1 Sample preparation

LiFePO₄/C composite cathode materials were prepared by sol-gel and gas-phase diffusion permeation method:the stoichiometric ratio of LiNO₃.H₂O,Fe (NO₃)3·9H₂O,and NH₄H₂PO₄ was 1:1:1.They were dissolved in the solution that mixed water with ethanol,either without carbon source or adding soluble carbon source (glucose,citric acid,and sucrose).Then,they were mixed evenly with a magnetic stirrer,continuing at 80℃for about 80 min until the sol appeared,then dried under 80℃,and the precursor of LiFePO₄/C was obtained.The diffusion experiments of LiFePO₄/C precursor were carried out in a small crucible gas-phase permeability furnace that we made ourselves,and the temperature was controlled by precise temperature controller (XMT-101).

Diffusion experiment [ 23] was pided into three steps:first,the gas-phase permeability furnace was heated to a preset temperature of 700℃ [ 24] for 30 min,using methanol as the diffusion agent,making the diffusion furnace in a reducing atmosphere;second,the LiFePO₄/C precursor was put into the furnace,regulating dripping speed of permeability agent to about 45 drops per minute;finally,LiFePO₄/C composite cathode materials were cooled down to room temperature after 7 h diffusion and LiFePO₄/C composite cathode material was obtained.

2.2.2 Battery assembly

Battery assembly process was conducted in a glove box filled with argon gas.Active substance acetylene black and polyvinylidene fluoride (PVDF) were weighed with the ratio of 75:15:10 (mass ratio).The mixed substances were dissolved in N-methyl pyrrolidone (NMP) and were evenly applied to the aluminum foil.After dried in a vacuum drying box under 120℃,it was punched into card,tablet,and detect battery.The electrode was lithium metal wafer with a diameter of 12 mm,a thickness of 100μm.The diaphragm was polypropylene with a diameter of 16 mm,a thickness of 16μm;the electrolyte consisted of ethylene carbonate (EC) and dimethyl carbonate (DMC),the volume ratio of which was EC:DMC=1:1 and the concentration of LiPF₆ was 1 mol·L^-1.

2.2.3 Cycle voltammetry (CV) characterization

The assembled simulation battery prepared by LiFePC₄/C material mixed 70%sucrose was scanned at voltage range of 2.5-4.3 V to test CV curve of the sample with scanning rate of 0.1 mV·s^-1.In the experiment,electrochemical workstation (CHI604C,Shanghai Chen Hua Company)was used.Test condition was two-electrode system.Auxiliary electrode and reference electrode were both lithium.The electrode was active sample electrode.

3 Results and discussion

3.1 Determination of gas-phase diffusion permeation temperature

LiFePO₄/C precursor without carbon source was tested by thermogravimetry-differential thermal analysis (TG-DTA)from room temperature to 800℃,and the heating rate was5℃·min^-1.The results were shown in Fig.1.It can be seen from the TG curve that the sample was at great loss from 80 to 600℃.The loss mainly occurred in three stages:the first stage was from room temperature to178℃,mainly removing the adsorbed water in the gel;the second stage was from 178 to 346℃,which was mainly because , and other small molecules decomposed;the third stage was from 346 to 605℃,and it was the main process of LiFePO₄/C crystal type changes.No weight loss occurred after 600℃,showing that the sample no longer had decomposition reaction after that temperature.According to the results of TG-DTA test,the diffusion temperature of LiFePO₄/C precursor is 700℃.

The TG-DTA test of LiFePO₄/C precursor with glucose as carbon source was carried out from room temperature to800℃,the heating rate was 5℃·min^-1 and the test results were shown in Fig.2.According to the TG curve,the sample had obvious weight loss from 80 to 600℃.Weight loss mainly occurred in three stages:the first stage was from room temperature to 178℃,mainly removing the adsorbed water in the gel;the second stage was from178 to 246℃,which was mainly caused by glucose decomposition;the third stage was from 246 to 600℃,and it was the main process of LiFePO₄/C crystal type changes.No weight loss after 600℃means that the sample no longer had decomposition reaction after that temperature.According to the results of TG-DTA test,the diffusion temperature of LiFePO₄/C precursor with glucose as carbon source is 700℃.

Fig.1 TG-DTA curves of LiFePO₄ precursor

The TG-DTA test of LiFePO₄/C precursor with 50%sucrose as carbon source was carried out from room temperature to 800℃,the heating rate was 5℃·min^-1.The test results were shown in Fig.3.According to the TG curve,the sample had obvious weight loss from 80 to600℃.Weight loss mainly occurred in three stages:the first stage was from room temperature to 125℃,mainly resulting from removal of the adsorbed water in the gel;the second stage was from 125 to 330℃,mainly caused by sucrose decomposition;the third stage was from 330 to610℃,which was the main process of LiFePO₄/C crystal type changes.No weight loss after 610℃shows that the sample no longer had decomposition reaction after that temperature.According to the test results of TG-DTA,the diffusion temperature of LiFePO₄/C precursor with sucrose as carbon source is 700℃.

The TG-DTA test of LiFePO₄/C precursor with 50%citric acid as carbon source was carried out from room temperature to 800℃,and the heating rate was5℃·min^-1.The test results were shown in Fig.4.According to the TG curve,the sample had obvious weight loss from 80 to 600℃.Weight loss mainly occurred in three stages:the first stage was from room temperature to160℃,mainly removing the adsorbed water in the gel;the second stage was from 160 to 350℃,mainly caused by citric acid decomposition;the third stage was from 350 to590℃,which was the main process of LiFePO₄/C crystal type changes.No weight loss after 600℃shows that the sample no longer had decomposition reaction after that temperature.According to the results of TG-DTA test,the diffusion temperature of LiFePOz₄/C precursor with citric acid as carbon source is 700℃.

Fig.2 TG-DTA curves of LiFePO₄/C precursor with glucose

Fig.3 TG-DTA curves of LiFePO₄/C precursor with sucrose

Fig.4 TG-DTA curves of LiFePO₄/C precursor with citric acid

Through the TG-DTA diagrams,it can be seen that different carbon source types determine different degrees of penetration.

3.2 XRD analysis

XRD patterns of the LiFePO₄/C sample prepared without carbon source and the LiFePO₄/C sample used glucose,citric acid,and sucrose as carbon source are shown in Fig.5.Compared with the standard spectrum (JCPD40-1499),all diffraction peaks were indexed to olivine structure.The results show that LiFePO₄/C prepared with different carbon sources have pure phase.No diffraction peaks appeared means that carbon exists in the form of amorphous carbon.Three peaks of all the samples were observed between 20°and 40°,among which LiFePO₄/C samples used citric acid as carbon source are the strongest.Angles of strong diffraction peaks of samples prepared with these four carbon sources are almost consistent.

Fig.5 XRD patterns of LiFePO₄/C synthesized by different carbon

3.3 SEM morphology analysis

The morphologies of LiFePO₄/C samples with different carbon sources are shown in Fig.6.From the chart,the grain size of the prepared sample is about 1μm with carbon coated.Samples without carbon source among the precursors are hardened to a certain extent.However,samples prepared by adding different carbon sources(glucose,sucrose and citric acid) to precursors have even particles.LiFePO₄/C sample with sucrose as the carbon source is the best among them as Fig.6c shows [ 25] .

3.4 Charge and discharge test

In order to study the effects of different carbon sources on the electrochemical properties of LiFePO₄/C samples,the LiFePO₄/C samples of button-type battery which were prepared with different carbon sources which were tested by charging and discharging.The first charge and discharge curves and cycle performance curves of samples without carbon source and with different carbon sources under0.5℃are shown in Figs.7 and 8.According to the Figures,the initial specific discharge capacity of LiFePO₄/C samples used glucose as carbon source is 64.80 mAh·g^-1and the initial discharge efficiency is 69.8%.As for LiFePO₄/C samples used citric acid as carbon source,the initial specific discharge capacity is 15.0 mAh·g^-1.The first specific discharge capacity of LiFePO₄/C samples prepared with sucrose as carbon source is 84.27 mAh·g^-1,and the initial discharge efficiency is 71.2%,higher than the initial efficiency (69.8%) of those used glucose as carbon source.The cycle performance is good,as well.After 30 cycles,the capacity retention rate is 94%,so LiFePO₄/C material is chosen as adding sucrose during the preparation of precursor.

Fig.6 SEM images of LiFePO₄/C synthesized by different carbon sources:a without carbon source,b glucose,c sucrose,and d citric acid

Fig.7 First discharge curves of LiFePO₄/C synthesized by different carbon sources

Fig.8 Cycle performance curves of LiFePO₄/C synthesized by different carbon sources

3.5 CV analysis

The symmetry of CV curve and redox peak area are important references of material cycle performance and the reversible capacity size.The better the symmetry of material circulation is,the greater the performance and the bigger the reversible capacity.The better the uniform of redox peak size is,the better cycle performance of the material and the greater reversible capacity of the assembled simulation battery.The curves of samples added with75%sucrose are consistent with the peak of charge and discharge.The charge peak is at 3.6 V,discharge peak is at3.25 V.The peak sharpness is better and the discharge peak area is consistent with charge peak area,showing the good reversible capacity and cycle performance of the material,as shown in Fig.9.

Fig.9 CV curve of LiFePO₄/C synthesized by 70 wt%sucrose

4 Conclusion

Pure-phase LiFePO₄/C materials were prepared by sol-gel and gas-phase diffusion permeation method.LiFePO₄/C precursor material prepared with glucose,sucrose,and citric acid as carbon source was diffused in diffusion furnace under 700℃,the diffusion time was 7 h.XRD,SEM,and charge-discharge test were used to analyze LiFePO₄/C materials prepared with different carbon sources.The results show that LiFePO₄/C material prepared with sucrose as carbon source has even particles with～1μm in diameter.The initial specific discharge capacity of the material is the highest at 84.27 mAh·g^-1 and has good cycle performance.After 30 cycles,the capacity retention rate is 94%,so the choice of carbon source for preparing LiFePO₄/C materials is sucrose.Owing to small electronic conductivity of LiFePO₄ and low speed of diffusion of lithium ion,the volume energy density is low,which severely affects the utility of the material.Therefore,using different methods to increase the conductivity of the LiFePO₄ material is the main research direction.

Acknowledgments This study was financially supported by the National Natural Science Foundation of China (No.51274143).

参考文献

[1] Padhi AK, Nanjundaswamy KS, Goodenough JB. Phospho-olivines as positive-electrode materials for rechargeable lithium batteries. J Electrochem Soc. 1997; 144(4):1188.

[2] Lin L, Ma XG, Guo Y, Wang Q, Xiao D. Study on preparation and electrochemical performance of LiFeP04 with microwave method. Res Appl Chem. 2010;22(5):570.

[3] Jiang ZJ. Development and challenge of LiFeP04 cathode materials for Li-ion batteries. J Funct Mater. 2010;3(41):365.

[4] Yang SF, Song YN, Peter Y, Zavalij M, Stanley W. Reactivity,stability and electrochemical behavior of lithium iron phosphates. Electrochem Commun. 2002;4(3):75.

[5] Zhang SH, Dou QS. Research progress of material preparation method of cathode material for lithium-ion batteries lithium iron cathode. Xinjiang Nonferrous Metals. 2009;62(S1):134.

[6] Yamada A, Chang SC, Hinokuma K. Optimized LiFeP04 for lithium battery cathodes. J Electrochem Soc. 2001;148(3):224.

[7] Hu J, Feng ZS, Wang Y, Chen JJ, Wang XJ. Study on the preparation of composite LiFePO_4/C cathode material mixing carbon doped by carbon thermal reduction method. Electron Compon Mater. 2013;32(11):23.

[8] Tang ZY, Qiu RL, Teng GP. Study of LiFeP04 cathode material for lithium ion battery. Chem Ind Eng Prog. 2008;27(7):995.

[9] Wang EX, Xu GR, Zheng HB, Zhang YX. An overview of coprecipitation method to synthesize LiFePO_4. Guangdong Chem Ind. 2011;38(1):97.

[10] Gao MY, Liu NQ, Li ZB, Li C. A gelatin-based sol-gel procedure to synthesize the LiFeP04/C nanocomposite for lithium ion batteries. Solid State Ion. 2014;34(6):8.

[11] Zhang HF, Sun Z, Chen MJ. Preparation and electrochemical performance of LiFePO_4 by microwave synthesis. Power Syst.2012;36(12):1787.

[12] Wang LL, Ma PH, Li FQ. The structure and the electrochemical reaction mechanism of LiFeP04 cathode material for lithium ion batteries. Chem Bull. 2008; 1(9):17.

[13] Zhong SK, Xu YB, Li YH, Zeng HH, Li W, Wang J. Synthesis and electrochemical performance of LiMnP04/C composites cathode materials. Rare Met. 2012;31(5):474.

[14] Hee PS, Hyoung KC. Preparation of Li[Ni1/3Co1/3Mn1/3]02powders for cathode material in secondary battery by solid-state method. Rare Met. 2006;25(6):186.

[15] Zhou JX, Shen XQ, Jing MX, Zhan Y. Synthesis and electrochemical performances of spherical LiFeP04 cathode materials for Li-ion batteries. Rare Met. 2006;25(6):20.

[16] Hamamoto K, Fukushima M, Mamiya M, Yoshizawa Y, Akimoto J, Suzuki T, Fujishiro Y. Morphology control and electrochemical properties of LiFeP04/C composite cathode for lithium ion batteries. Solid State Ion. 2012;225(14):562.

[17] Kim JK, Choi JW, Cheruvally G, Ahn JH. A modified mechanical activation synthesis for carbon-coated LiFePO_4cathode in lithium batteries. Mater Lett. 2007;61(18):3822.

[18] Cao YL, Yu LH, Li T, Yang HX. Synthesis and electrochemical characterization of carbon-coated nanocrystalline LiFeP04 prepared by polyacrylates-pyrolysis route. J Power Sources. 2007;172(2):1.

[19] Neelima M, Amitava B, Alka G, Shobit O, Kantesh B. Progress in material selection for solid oxide fuel cell technology:a review. Prog Mater Sci. 2015;72(7):145.

[20] Zhang YH, Cai Y, Li BW, Ren HP, Hou ZH, Zhao DL. Electrochemical hydrogen storage characteristics of the as-cast and annealed La_(0.8-x)Pr_xMg_(0.2)Ni_(3.35)A_(10.1)Si_(0.05)(x=0-0.4)electrode alloys. Rare Metal Mater Eng. 2013;42(10):1985.

[21] Wang GX, Zhang XH, Han ES, Wang CX. Study on electrochemical performance of LiFeP04 cathode materials mixing different carbon sources. Inorg Salt Chem Ind. 2008;41(8):35.

[22] Prosini PP, Carewska M, Scaccia S, Pasquali M. Long-term cyclability of nanostructured LiFeP04. Electrochim Acta. 2003;48(28):4205.

[23] Xu J, Chen G, Xie CD. Synthesis and electrochemical performance of LiFeP04/C prepared by a new method. Solid State Commun. 2008;147(11-12):443.

[24] Peng ZD, Cao YB, Zhou YL, Hu GR. Synthesis of LiFeP04using FeS04-7H20 byproduct from Ti02 production as raw materials. Rare Met. 2009;28(6):612.

[25] Luo WB, Wen L, Luo HZ, Song RS, Zhai YC, Liu C, Li F.Carbon nanotube-modified LiFeP04 for high rate lithium ion batteries. New Carbon Mater. 2014;29(4):292.