Rolling texture and its effect on tensile property of a near-α titanium alloy Ti60 plate
来源期刊:JOURNAL OF MATERIALS SCIENCE TECHNOLOG2019年第5期
论文作者:Wenyuan Li Zhiyong Chen Jianrong Liu Shaoxiang Zhu Guoxin Sui Qingjiang Wang
文章页码:790 - 798
摘 要:Rolling texture and its effect on tensile properties of Ti60 alloy plates were investigated in the present study. The plates wereβ-rolled at 1070℃ and(α+β)-rolled at 980℃, using uni-directionally rolling(UDR) and cross-directionally rolling(CDR) processes, respectively.β-rolled plates exhibited weak textures, which were attributed to the dispersive orientations of secondary α during the β→α phase transformation. Strong deformation textures formed in(α+β)-rolled plates as a result of slipping mechanisms: the strong T-type texture in UDR plate was related to {10 1 0}[11 2 0] slipping, while the B-type texture in CDR plate was relevant with {0001}[11 2 0] slip. Strong T-type textures led to anisotropic tensile properties. B-type textures would decrease such an anisotropy. The(α+β)-CDR process was found to be a candidate process for reducing anisotropy of Ti60 alloy plates.
Wenyuan Li1,2,Zhiyong Chen1,Jianrong Liu1,Shaoxiang Zhu1,Guoxin Sui1,Qingjiang Wang1
1. Institute of Metal Research, Chinese Academy of Sciences2. University of Chinese Academy of Sciences
摘 要:Rolling texture and its effect on tensile properties of Ti60 alloy plates were investigated in the present study. The plates wereβ-rolled at 1070℃ and(α+β)-rolled at 980℃, using uni-directionally rolling(UDR) and cross-directionally rolling(CDR) processes, respectively.β-rolled plates exhibited weak textures, which were attributed to the dispersive orientations of secondary α during the β→α phase transformation. Strong deformation textures formed in(α+β)-rolled plates as a result of slipping mechanisms: the strong T-type texture in UDR plate was related to {10 1 0}[11 2 0] slipping, while the B-type texture in CDR plate was relevant with {0001}[11 2 0] slip. Strong T-type textures led to anisotropic tensile properties. B-type textures would decrease such an anisotropy. The(α+β)-CDR process was found to be a candidate process for reducing anisotropy of Ti60 alloy plates.