Effect of Chromium Micro-alloying on the Corrosion Behavior of a Low-carbon Steel Rebar in Simulated Concrete Pore Solutions
来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2017年第6期
论文作者:宋丹 蒋金洋 孙伟 MA Han ZHANG Jianchun CHENG Zhaojun JIANG Jinghua AI Zhiyong
文章页码:1453 - 1463
摘 要:A new low-cost corrosion-resistant rebar(HRB400 R) was designed and fabricated by chromium micro-alloying. The effects of Cr on the passivation and corrosion behavior of this rebar in the simulated concrete pore solutions were studied systematically, and its improved corrosion resistance was revealed. In the Cl--free saturated Ca(OH)2 solution, the HRB400 R rebar presented nearly the same passive film and similar passivation ability compared to the common carbon steel rebar. In the long-term immersion corrosion test in the Cl--contained Ca(OH)2 solution, the HRB400 R rebar presented improved corrosion resistance and obvious longer passivation-maintaining period. Micro-alloying of Cr element in the rebar matrix enhanced its corrosion resistance against Cl--attack and retarded the corrosion initiation in the matrix. In the alkaline Na Cl salt spraying test, the HRB400 R rebar also presented obviously lower mass-loss rate. The enrichment of Cr element in the rust layer improved its retardant effect to the penetration of aggressive medium, and decreased the corrosion propagation rate of the rebar.
宋丹1,2,3,4,蒋金洋1,孙伟1,MA Han5,ZHANG Jianchun5,CHENG Zhaojun3,JIANG Jinghua3,AI Zhiyong1
1. School of Materials Science and Engineering, Southeast University2. Nantong Ocean and Coastal Engineering Research Institute, Hohai University3. College of Mechanics and Materials, Hohai University4. Suqian Research Institue, Hohai University5. Jiangsu Shagang Group Co. Ltd
摘 要:A new low-cost corrosion-resistant rebar(HRB400 R) was designed and fabricated by chromium micro-alloying. The effects of Cr on the passivation and corrosion behavior of this rebar in the simulated concrete pore solutions were studied systematically, and its improved corrosion resistance was revealed. In the Cl--free saturated Ca(OH)2 solution, the HRB400 R rebar presented nearly the same passive film and similar passivation ability compared to the common carbon steel rebar. In the long-term immersion corrosion test in the Cl--contained Ca(OH)2 solution, the HRB400 R rebar presented improved corrosion resistance and obvious longer passivation-maintaining period. Micro-alloying of Cr element in the rebar matrix enhanced its corrosion resistance against Cl--attack and retarded the corrosion initiation in the matrix. In the alkaline Na Cl salt spraying test, the HRB400 R rebar also presented obviously lower mass-loss rate. The enrichment of Cr element in the rust layer improved its retardant effect to the penetration of aggressive medium, and decreased the corrosion propagation rate of the rebar.
关键词: