Rare Metals 2013,32(03),305-311+2
Current efficiency in electro-winning of lanthanum and cerium metals from molten chloride electrolytes
Deepak Kumar Sahoo Harvinderpal Singh Nagaiyar Krishnamurthy
Rare Earths Development Section, Bhabha Atomic Research Centre
Fusion Reactor Materials Section, Bhabha Atomic Research Centre
摘 要:
The objective of this study is to prepare lanthanum and cerium metals by fused salt electrolysis of their anhydrous chloride in molten media such as LiCl-KCl, NaCl-KCl, KCl, NaCl, and LiCl and to characterize the metal deposit by X-ray diffraction, energy dispersive X-ray fluorescence, and inductive coupled plasma-atomic emission spectroscopy. Deposit metal of purity more than 99 % was obtained in each of the experiments. The entire process starting from preparation of anhydrous lanthanum/cerium chloride to electrolysis yielding of metal deposits has been described. The effect of process parameters such as temperature, electrolyte composition, and current density on the current efficiency was studied. All these parameters were varied to get the highest current efficiency and metal yield. The major non-rare earth impurities with the deposit are found to be Fe, Cr, and Ni along with ~1×10-3 of total gaseous impurities.
作者简介:Deepak Kumar Sahoo e-mail:deesahoo@gmail.com;
收稿日期:9 November 2012
Current efficiency in electro-winning of lanthanum and cerium metals from molten chloride electrolytes
Abstract:
The objective of this study is to prepare lanthanum and cerium metals by fused salt electrolysis of their anhydrous chloride in molten media such as LiCl–KCl, NaCl–KCl, KCl, NaCl, and LiCl and to characterize the metal deposit by X-ray diffraction, energy dispersive X-ray fluorescence, and inductive coupled plasma-atomic emission spectroscopy. Deposit metal of purity more than 99 % was obtained in each of the experiments. The entire process starting from preparation of anhydrous lanthanum/cerium chloride to electrolysis yielding of metal deposits has been described. The effect of process parameters such as temperature, electrolyte composition, and current density on the current efficiency was studied. All these parameters were varied to get the highest current efficiency and metal yield. The major non-rare earth impurities with the deposit are found to be Fe, Cr, and Ni along with ~1×10-3 of total gaseous impurities.
Keyword:
Fused salt electrolysis; Current density; Current efficiency; Rare earths;
Received: 9 November 2012
1 Introduction
Rare earth metals possess some unique physical and metallurgical properties that make them valuable functional materials in devices for electronic,magnetic,superconductor,and hydrogen storage applications[1–4].Rare earth metals impart desirable mechanical and corrosion resistance properties in a number of ferrous and nonferrous metals and alloys[5–7].Cerium and lanthanum are the most abundant rare earth elements available in the ores of monazite and bastenite.These metals are very reactive and they form very stable oxides.A wide variety of precursors ranging from oxides to chlorides and fluorides are used in preparing these metals.Due to the strong electropositive character of these metals,chemical reduction with the common reducing agents is not possible.Strong reducing agents such as calcium is required for oxide and for halides,calcium and lithium are effective.Therefore,the practical methods for preparation of these metals are limited to techniques such as calciothermic reduction and electro-winning.Fused salt electrolysis process for making these metals is attractive because of low cost,ease of operation,batch size,and the purity of the product Moreover,fused salt electrolysis becomes particularly attractive for these(La and Ce)metals,because their melting point facilitates their electro-winning in molten state,which eventually yields a product with minimum contamination.Various investigations have been reported for electro-winning of lanthanum and cerium in both chloride and fluoride baths[8–12].Although fluoride salt is stable in air compared with chloride,which is hygroscopic the advantages of chloride are ease of preparation and lowmelting temperature.
The carrier electrolytes used in this process are mostly alkali and alkaline halides,which have good solubility for rare earth metal halides.The low hygroscopicity of alkali halides makes them more favored over alkaline halides Li Cl–KCl and Na Cl–KCl are the most common flux used for this purpose[13].In this process,various factors including temperature,current density(for both cathode and anode),and duration of electrolysis can affect the outcome of the product.However,data on the effects of temperature,bath composition,duration,and current densities are limited in the literature.The objective of this study is to observe the effect of process parameters in Li Cl–KCl and Na Cl–KCl baths and to investigate the effect of using single carrier electrolyte such as KCl,Na Cl,and Li Cl in preparing lanthanum and cerium metals.
2 Experimental
The starting materials used lanthanum and cerium oxides([99%pure)obtained from Indian Rare Earths Ltd.Potassium chloride,sodium chloride,and lithium chloride having 99.5%purity of LR grade were procured from the local market.Molybdenum rod of 99%purity and highdensity graphite(q=1.82 9 103kg?m-3)crucibles were used as cathode and anode,respectively.
The first step in the overall process is the conversion of La/Ce oxides to their corresponding chlorides.The oxides were dissolved in hot hydrochloric acid(50%strength)with constant stirring until the crystallization occured[14].The temperature of the solution was maintained within353–373 K.The product obtained was examined by X-ray diffraction(XRD)analysis and found to be La/Ce Cl3?7H2O.Dehydration of La Cl3?7H2O was carried out by stepwise heating to 523 K for 24 h in dynamic vacuum and the escaping water vapor was collected by using a liquid nitrogen trap.Mixture of Li Cl–KCl(in 1:1 weight ratio)was also dehydrated at 523 K for 4 h to remove adsorbed moisture.The mixture of anhydrous La Cl3with Li Cl–KCl taken in a required proportion was used as electrolyte for lanthanum metal deposition.Experiments were also conducted in Na Cl–KCl bath in place of Li Cl–KCl flux.The electrolytic mixture taken in each experiment was 1 kg with different concentrations of La Cl3,keeping the weight ratio of Li Cl/Na Cl:KCl constant(i.e.,1:1).Similar experiments were carried to electro-win cerium metal from Ce Cl3using Li Cl–KCl and also with Na Cl–KCl carrier electrolyte separately.
The electrolytic mixture was charged into a 0.7 m diameter and 0.25 m tall graphite crucible,which served the purpose of container material as well as anode.A molybdenum rod of 0.6 mm diameter used as cathode was sheathed by a close-fitting alumina tube stuffed with asbestos rope,except the portions required to see the electrolyte in the lower part and for cathode connection in the upper part.The role of alumina sheath was to give electrical insulation and also to prevent molybdenum rod from getting corroded with Cl2gas,which forms during electrolysis.A schematic diagram of the electrolytic cell assembly is shown in Fig.1.It consists of a vacuum tight Inconel retort(0.1 m diameter)fitted with a stainless steel flange system having provision for placing the cathode rod and thermocouple and for gas inlet and outlet.The negative terminal of DC power supply is connected to Mo rod and positive terminal to Inconel retort,which eventually makes graphite as anode.To collect the material deposited at cathode,an alumina crucible was placed below the cathode inside the graphite crucible.The alumina crucible and cathode rod were kept in such a manner that the tip of the molybdenum rod was just above the alumina crucible.The graphite crucible was placed in the Inconel retort,which was kept in a tubular vertical resistance furnace as shown in Fig.1.The resistance furnace with temperature electronic control(±1 K)was used to heat the cell up to the operating temperature.The electrolyte in the graphite crucible was melted in high pure argon gas.The role of argon gas is also to prevent the oxidation of cell material The temperature of the bath was measured with a K-type thermocouple protected by an alumina well inserted into the melt.After equilibrating the bath for 1 h,the cathode was lowered and pre-electrolysis was carried out to remove residual water followed by electrolysis applying potential of 5–8 V from a DC power supply.Electrolysis was continued for a specific period of time,and after electrolysis the cell was allowed to cool to room temperature in an argon atmosphere.Molybdenum rod and thermocouples were taken above the electrolytic bath to prevent them from sticking inside the salt,which solidifies on cooling The molten metal collected in the alumina crucible was recovered by washing solidified molten salt with water The alumina being nonconducting helped to protect the metal from anodic attack,as well as reaction with graphite crucible.The amount of metal collected in each experiment was 0.2–0.3 kg according to the amount of functional electrolyte.
Similar experiments were also carried out using only one solvent such as KCl,Li Cl,and Na Cl to study effect of change in carrier electrolyte on the process and yields.Products were analyzed by X-ray diffraction(XRD),energy dispersive X-ray fluorescence(EDXRF),and inductive coupled plasma-atomic emission spectroscopy(ICP-AES).
![](/web/fileInfo/upload/magazine/14764/369739/XYJS201303018_16100.jpg)
Fig.1 Scheme of electrolyte cell
3 Results and discussion
3.1 Electrolytic reaction
The cell can be represented as follows:
C?graphite?;Cl2?gas?j La Cl3?Li Cl?KClj La3?=La;Mo At cathode?Mo?;La3??3e?!La
At anode?graphite?;3Cl?!3=2Cl2?3e?
3.2 Characterization of metal
In the first step,the lanthanum and cerium metal products were characterized by XRD.Figures 2 and 3 show the XRD pattern of cerium and lanthanum metals.All the diffracted peaks well match with their corresponding PCPDF patterns of 36-0815 and 78-0638,respectively.No diffraction from any impurities is found,indicating the impurities below X-ray detection limit.
EDXRF patterns of cerium and lanthanum metals are shown in Figs.4 and 5.From these spectra,it is clearly observed that the major peaks belong to lanthanum and cerium metals,with some peaks of other elements such as Ni,Cr,and Fe.
Chemical analysis results given in Table 1 show the quantitative picture of metal purity.From Table 1,it is clearly observed that the metal purity obtained in each experiment is more than 99%.The iron,chromium,and nickel impurities vary from 0.1 wt%to 0.3 wt%.The chromium impurity mostly comes from molybdenum cathode,which contains*0.5 wt%chromium.The impurities of iron and nickel probably come from the salt mixture of alkali chlorides.By using higher purity chemicals and electrodes,it is probably possible to get these metals in higher purity state.The gaseous impurities of hydrogen,nitrogen,and oxygen are found in1 9 106level.These impurities may be avoided by using high-pure argon gas as protective atmosphere instead of commercial grade of argon as used in our experiments.
![](/web/fileInfo/upload/magazine/14764/369739/XYJS201303018_17100.jpg)
Fig.2 XRD pattern of electrodeposited Ce metal
![](/web/fileInfo/upload/magazine/14764/369739/XYJS201303018_17200.jpg)
Fig.3 XRD pattern of electrodeposited La metal
![](/web/fileInfo/upload/magazine/14764/369739/XYJS201303018_17300.jpg)
Fig.4 EDXRF pattern of electrodeposited Ce metal
![](/web/fileInfo/upload/magazine/14764/369739/XYJS201303018_17400.jpg)
Fig.5 EDXRF pattern of electrodeposited La metal
Table 1 Evaluation of metal purity 下载原图
![](/web/fileInfo/upload/magazine/14764/369739/XYJS201303018_17500.jpg)
Table 1 Evaluation of metal purity
3.3 Relation between electrolytic temperature and current efficiency
The effect of temperature on current efficiency(CE)is shown in Figs.6 and 7.Metals were obtained by electrolysis in the electrolytic bath containing 40 wt%La Cl3/Ce Cl3with equimolar ratio of Na Cl and KCl.All these experiments were carried out at a constant current density of 1 9 105A?m-2for 3 h.From Fig.6,it is clearly seen that,with the increase of electrolysis temperature,current efficiency for cerium metal increases and reaches maximum value and thereafter started falling.Owing to high viscosity of electrolyte at lower temperature electrical conductivity,and mobility of ions is low at low temperature,the diffusion movement electro-active species is slow,which is unfavorable in improving the current efficiency.With the increase of temperature,increased diffusion kinetics gives higher current efficiency.However,after a certain optimum temperature,the current efficiency begins to decrease due to increased solubility of cathode deposit in the melt[15],as well as higher volatilization of the electrolyte.The optimum temperature for electro-winning of cerium is 1,163 K.In the case of lanthanum,the operational temperature is high,as its melting point of 1,194 K is higher than that of cerium,whose melting point is 1,080 K.Owing to high operational temperature,CE is maximum due to enhanced diffusion kinetics of lanthanum ion.On further increase in temperature,efficiency decreases due to increase in solubility of metal in the melt.The optimum temperature for lanthanum deposition is found to be1,213 K.
3.4 Effect of concentration of functional electrolyte on CE
The effect of change in concentration of La/Ce Cl3on CE is shown in Fig.8.Here,the mass fraction of Ln Cl3varies under a cathode current density(CCD)of 7 9 104A?m-2Operating temperature for lanthanum and cerium were1,213 and 1,163 K,respectively.At low concentration of functional electrolyte,CE is low due to preferential reduction of solvent ions compared with functional ions according to Nernst equation.With increase in concentration,CE starts increasing due to availability of more lanthanide ions around cathode.This is substantiated by observing improvement in CE by increasing concentration of RECl3in the electrolyte up to 50 wt%.Further increase in the concentration of metal chloride makes the bath more viscous,which decreases the conductivity of molten electrolyte and hence decreases the CE.Therefore,the optimum concentration of Ln Cl3in both lanthanum and cerium cases appears to be 50 wt%.It is evident from the Fig.8that CE for cerium metal is lower than that of lanthanum metal.Cyclic oxidation and reduction between Ce(III)and Ce(IV)are presumed to be the reason for low CE in cerium[9].
3.5 Effect of CCD on CE
The relationship between CCD and CE was studied for both La and Ce metal deposition in Li Cl–KCl and Na Cl–KCl baths.Figure 9 shows the variation of CE in the CCD range of(4–10)9 104A?m-2for both La Cl3–Na Cl–KCl and La Cl3–Li Cl–KCl.Similarly,Fig.10 shows the variation of CE in the CCD range of(4–16)9 104A?m-2both for Ce Cl3–Na Cl–KCl and Ce Cl3–Li Cl–KCl.The Ln Cl3content in each case is 50 wt%.Operational temperature for cerium is 1,163 K and that of lanthanum is 1,213 K.
![](/web/fileInfo/upload/magazine/14764/369739/XYJS201303018_18200.jpg)
Fig.6 CE at different temperatures of operation for Ce metal
![](/web/fileInfo/upload/magazine/14764/369739/XYJS201303018_18300.jpg)
Fig.7 CE at different temperatures of operation for La metal
![](/web/fileInfo/upload/magazine/14764/369739/XYJS201303018_18400.jpg)
Fig.8 Effect of concentration of RECl3on CE
Both Figs.9 and 10 show that CE increases with the increase of CCD.On increasing the current density,the kinetics of migration of lanthanide ions increases due to the increase of cathodic potential,which helps in depositing metals at a greater speed and thus increases the CE However,a very high-current density results in the codeposition of flux ions due to high-negative potential of cathode,which reaches the deposition potential of flux ions.The optimum CCD for lanthanum deposition is8 9 104A?m-2in both Li Cl–KCL and Na Cl–KCl melts For cerium,the optimum CCD is 10 9 104A?m-2in Li Cl–KCl melt and 12 9 104A?m-2in Na Cl–KCl melt.
![](/web/fileInfo/upload/magazine/14764/369739/XYJS201303018_18600.jpg)
Fig.9 Influence of current densities on CE for Ce metal in Li Cl–KCl and Na Cl–KCl flux
![](/web/fileInfo/upload/magazine/14764/369739/XYJS201303018_18700.jpg)
Fig.10 Influence of current densities on CE for La metal in Li Cl–KCl and Na Cl–KCl flux
3.6 Effect of changing the carrier electrolyte
Figures 9 and 10 give the comparison picture of effect of CCD on CE for both metals in Li Cl–KCl and Na Cl–KCl solvents.The range of stability and greater fluidity of Li Cl–KCl over Na Cl–KCl solvent shows the CE trend in Figs.9and 10.It is found that,at lower current density,there may be a significant difference in CE,but at higher current density this difference is negligible.At lower current density,CE for cerium metal,in particular,is low,which may be attributed to cyclic oxidation and reduction of Ce3?and Ce4?.This is contradictory to the Ref.[16],which reported that reduction of Ce(III)to Ce(0)was a single-step process.Low CE for Ce at low CCD could be due to lowinternal mobility of cerium ion compared with lanthanum ion[17].The increase of mass transfer rate at a higher current density leads to higher CE values for both Li Cl–KCl and Na Cl–KCl baths.From the industrial production point of view,Na Cl–KCl has the advantage over Li Cl–KCl due to its low cost.
![](/web/fileInfo/upload/magazine/14764/369739/XYJS201303018_19000.jpg)
Fig.11 Variation of CE on using inpidual flux for cerium metal
![](/web/fileInfo/upload/magazine/14764/369739/XYJS201303018_19100.jpg)
Fig.12 Variation of CE on using inpidual flux for lanthanum metal
The preparation of metals is also possible using only inpidual flux such as KCl,Na Cl,or Li Cl.In these cases,applied voltage in the electrolysis is slightly higher than the Li Cl–KCl or Na Cl–KCl flux.The CEs obtained in these cases are comparable with that obtained in mixture solvent.The purity of metal and amount of flux metal obtained here is also comparable with that of prepared in mixed solvent as evident from Table 1.Another interesting factor is found here:CE decreases from KCl to Na Cl and to Li Cl for both metals as shown in Figs.11 and 12.Although this trend is not fully understood,it is believed to be due to the slow mass transfer of lanthanide ions in Na Cl and Li Cl compared with KCl melt.It could be due to the formation of higher-order lanthanide complex in the presence of Na Cl and Li Cl[18–23].Further studies are definitely required to predict the mechanism for this observed trend.
4 Conclusion
Cerium and lanthanum metals with more than 99%purity were prepared in batches of 0.3 kg each.All the process parameters were varied to get high CE and yield for both these metals in Li Cl–KCl and Na Cl–KCl baths.CE of87%and 90%are obtained in preparing Ce and La metal respectively,by operating the electrolytic cell under best conditions.The suitable temperature for electro-winning of cerium and lanthanum is found to be 1,163 and 1,213 K respectively.The optimum CCD for lanthanum deposition is 8 A?cm-2in both Li Cl–KCL and Na Cl–KCl melts.For cerium,the optimum CCD is 10 A?cm-2in Li Cl–KCl melt and 12 A?cm-2in Na Cl–KCl melt.Preparations of these metals were also carried out using inpidual flux of KCl Li Cl,and Na Cl.Maximum CE and yield were observed in KCl compared with Na Cl or KCl flux for both the metals
参考文献
[1] Chakoumakus Bryan C,Sales Brian C,Mandrus David,Keepens Veerle.Disparate,atomic displacements in skutterudite-type LaFe3CoSb12,a model for thermoelectric behavior.Acta Crys-tallogr B.1999;B55(3):341.
[2] Sarkis Angie,Callen Earl.Magnetic anisotropy of rare earths-transition metal compounds.Phys Rev B.1982;26(7):3870.
[3] Soto F,Cabo L,Mosqueira J,Ramallo MV,Veira JA,Vidal F.Observation of enhanced fluctuation of diamagnetism in lan-thanum superconductors with dilute magnetic impurities.Euro-phys Lett.2006;73(4):587.
[4] Konishi H,Yoshihara Y,Ono H,Usui T,Oishi T,Nohira T.Electrochemical formation and phase control of La–Ni alloy films in LiCl–KCl melts.J Jpn Soc Exp Mech.2010;10(SI):215.
[5] Jain C-C,Koo C-H.Creep and corrosion property of the extruded magnesium alloy containing rare earth.Mater Trans.2007;48(2):265.
[6] Fukumoto M,Yamashita R,Hara M.Improvement in oxidation resistance of stainless steel by molten salt electrodeposition of La.Oxid Met.2004;62(5–6):309.
[7] Hughes AE,Gorman JD,Paterson PJK.Characterization of Ce–Mo based conversion coatings on Al alloys.Corros Sci.1996;38(11):1957.
[8] Yamamura T,Mehmood M,Maekawa H,Sato Y.Electro-chemical processing of rare-earth and rare metals by using molten salts.Chem Sustain Dev.2004;12(1):5.
[9] Singh S,Pappachan AL,Gadiyar HS.Electrodeposition of cer-ium and Ce–Co alloy.J Less Common Met.1968;120(2):307.
[10] Singh S,Pappachan AL.Electrowinning of cerium group metal from fused chloride bath.Bull Mater Sci.1980;2(3):155.
[11] Constantin V,Popescu AM,Zuca S,Gaune-Escard M,Olteanu M.Electrochemical studies on cerium(III)in molten fluoride mixture.J Rare Earths.2010;28(3):428.
[12] Kaneko A,Yamamoto Y,Okada C.Electrochemistry of rare earth fluoride molten salt.J Alloys Compd.1993;193(1–2):44.
[13] Gupta CK,Krishnamurthy N.Extractive metallurgy of rare earths.Int Mater Rev.1992;37(5):197.
[14] Gaune-Escard M,Bogacz A,Rycerz L,Szczepaniak W.Heat capacity of LaCl3,CeCl3,PrCl3,NdCl3,GdCl3,DyCl3.J Alloys Compd.1996;235(2):176.
[15] Feng L,Guo C,Tang D.Relation between the dissolution behavior and current efficiencies of La,Ce,Pr and Nd in their chloride molten salts.J Alloys Compd.1996;234(2):183.
[16] Castrillejo Y,Bermejo MR,Pardo R,Martinez AM.Use of electrochemical techniques for the study of solubilization of cerium-oxide compounds and recovery of metal from molten chlorides.J Electroanal Chem.2002;522(2):124.
[17] Zablocka-Malicka M,Szczepaniak W.Internal mobility of Ln3?ions in KCl–LnCl3and NaCl–NdCl3systems.A single coeffi-cient correlation model.J Mol Liq.2008;137(1–3):36.
[18] Matsumiya M,Seo K.A molecular dynamics simulation of the transport properties of molten(La1/3,K)Cl.Z J Nat Res A.2005;60:187.
[19] Kushkhov KhB,Vindizheva MK,Karashaeva RA.Electrore-duction of cerium ions on silver electrode in halide melts at973K.Russ J Electrochem.2006;42(8):830.
[20] Photiadis GM,Borresen B,Papatheodorou GN.Vibrational modes and structures of lanthanide halide–alkali halide binary melts.J Chem Soc Faraday Trans.1998;94:2605.
[21] Okamoto Y,Shiwaku H,Yaita T,Narita H,Tanida H.Local structure of molten LaCl3by K-absorption edge of XAFS.J Mol Struct.2002;641:71.
[22] Mukherjee A,Gulnar AK,Sahoo DK,Krishnamurthy N.Gas solid techniques for preparation of pure lanthanum hexaboride.Rare Met.2012;31(3):285.
[23] Wang N,Huang K,Hou J,Zhu H.Preparation of niobium nanoparticles by silicothermic reduction of Nb2O5in molten salts.Rare Met.2012;31(6):621.